Abstract:Ni-Co alloy coating is applied to crystallizer surface to enhance its wear resistance for continuous steel casting. This study investigated the effects of heating temperature on the hardness, strength, and elongation of Ni-21 wt% Co coatings obtained by electroplating. The evolution of microstructure was analyzed by scanning electron microscopy, transmission electron microscopy, and X-ray diffraction. The results indicated that the as-deposited coating had a mixed structure of nanocrystals and microcrystals, containing numerous nanotwins and stacking faults. Its hardness, tensile strength, yield strength, and elongation were 371 HV0.1, 1170 MPa, 1117 MPa, and 13.8 %, respectively. After low-temperature heating, the number of nanocrystals decreased, whereas the fraction of microcrystals increased. At heating temperatures of 100-200 degrees C, a reverse Hall-Petch phenomenon occurred owing to the formation of annealing twins and the transformation of dislocation-emission mechanisms, resulting in a stable hardness and tensile strength. As the heating temperature was further increased, the grains continuously grew, thereby decreasing the hardness and tensile strength. After annealed at 400 degrees C, the elongation reached 32.5 %, whereas the hardness, tensile strength, and yield strength decreased to 200 HV0.1, 662 MPa, and 577 MPa, respectively.

The Structure and Microhardness of Ni-Fe-P and Ni-Fe-P-B Alloy Deposits Prepared by Electroless Plating

Structure and Property of Ni-W-B Alloy Electrodeposits Before and after Heat Treatment

Preparation and Properties of Textured Ni–W Coatings Electrodeposited on the Steel Surface from a Pyrophosphate Bath

Effects of heat-treatment temperature on microstructure and electrochemical properties of AB5 type MlNi 3.60Co 0.85Mn 0.40Al 0.15 hydride electrode alloy

Electrodeposition of Ni-W-P alloy

Electrodeposition and Properties of an Amorphous Ni-W-B Alloy Before and after Heat Treatment

Effects of annealing temperature on the crystal structure and properties of electroless deposited Ni–W–Cr–P alloy coatings

PREPARATION AND PROPERTIES OF BULK AMORPHOUS Fe-Ni-P-B-Ga ALLOYS

Synthesis, Composition, Morphology, and Wettability of Electroless Ni-Fe-P Coatings with Varying Microstructures

Microstructure and Crystallization Process of Electrodeposited Amorphous Ni-P Coatings

The Structure and Properties of Electroless Ni–Mo–Cr–P Coatings on Copper Alloy

Microstructures of electroless Ni–P alloy deposits and their transformation sequences during post-deposition annealing

Phase Transformation Sequence of Mixed-Structural Electroless Ni-19.7at.% P Deposit

Structure Transformations and Property of Electroless Ni-B Coating

Electrocrystallization Mechanism Structure and Microhardness of Ni-W-P Alloy Eletrodeposits

AFM analysis on the surface of electroless Ni-B coating

The Heat Treatment Effect on Microstructure and Dynamic Mechanical Properties of Electroformed Nanocrystalline Ni–W Alloy

Study of Heat Stability of Ni-W Alloys Film for Micro-Devices

INFLUENCE OF SURFACE MORPHOLOGY ON THE MICROHARDNESS OF ELECTROLEESS NI-B DEPOSIT REVEALED BY AFM OBSERVATION

Evolution of Microstructure and Mechanical Properties of Electroplated Nanocrystalline Ni–Co Coating During Heating

Studies on structure of electroless Ni-P alloy