Enhanced Jc in Bi-2212 Round Wires with Optimization of Calcination Atmosphere

L. H. Jin,Z. K. Xiong,X. Y. Xu,G. Q. Liu,J. Q. Feng,S. N. Zhang,Q. B. Hao,C. S. Li,P. X. Zhang
DOI: https://doi.org/10.1109/tasc.2023.3335878
IF: 1.9489
2024-01-01
IEEE Transactions on Applied Superconductivity
Abstract:High-performance precursor powders are crucial for the transport current of Bi 2 Sr 2 CaCu 2 O x (Bi-2212) round wires. However, the impact of the powder calcination process on the wire performance is not fully understood. Here, Bi-2212 precursor powders were prepared using ultrasonic spray pyrolysis technique and then calcined under different atmospheres. The influences of calcination atmosphere on the microstructures, melting behavior and critical current density ( J c ) of Bi-2212 multi-filamentary wires were systematically discussed by tuning the oxygen partial pressure from 0.001 bar to 1.0 bar. As the oxygen partial pressure was increased, a more uniform melting behavior was observed in the Bi-2212 wires, and the large merging bridges was reduced in the filaments. High J c of 2715 A/mm 2 at 4.2 K, 12 T were achieved in the sample with 1.0 bar O 2 . Therefore, controlling calcination atmosphere of precursor powder was significant for achieving superior transport current of Bi-2212 wires.
What problem does this paper attempt to address?