Abstract:Abstract. Micron-sized WC-metal (WC-0.6%C-21%Cr-6%Ni) powder was coated onto the substrate of magnetic bearing shaft material Inconel718 (substrate or In718) using JK3500 HVOF thermal sprayer for the improvement of the surface properties of the substrate. The optimal coating process for the highest surface hardness was obtained using the Taguchi experimental program. The coating was laser heat-treated (LH) by CO2(g) laser for further improvement of the properties. During the thermal spraying, a small portion of metal carbides of powder decomposed to W2C, metals and free carbon. The free carbon reacted with excessively sprayed oxygen, and formed carbon oxide gases, forming porous coating. By laser-heating, porosity decreased and the porous strips at the interface of coating and substrate (coat/sub) compacted. At the interface, the precipitated graphite concentration decreased and the metal elements diffused from both the coating and substrate increased, enhancing the functions as buffer zone and increasing adhesion of coating. The surface hardness of substrate increased by coating and further increased by laser-heating from 410±30 Hv to 983±101 Hv and 1425±94 Hv respectively. Porosity of coating decreased by laser-heating from 2.6±0.4% to 0.35±0.06%, and coating thickness shrank from 280μm to 200μm. Friction coefficients of substrate decreased from 0.52±0.02 to 0.36±0.04 by coating, because the free carbon formed by decomposition of WC to W2C functioned as a solid lubricant. By increasing sliding surface temperature from 25°C to 450°C, the friction coefficients of substrate and coating were decreased from 0.52±0.02 to 0.31±0.02 and from 0.36±0.04 to 0.23±0.04 respectively, because of easy formation of free carbon and metal oxides which functioned as solid lubricants. Wear depth of surface was decreased by coating and by LH coating from 55μm to 32 μm and to 12 μm respectively. HVOF coating of WC-metal powder on In718 surface and laser heat-treatment of the coating are highly recommended for the improvement of the properties of magnetic bearing shaft.

Interface Strengthening for Thermal Sprayed WC-10Co4Cr Coating Subjected to Pulsed Magnetic Treatment

Electrochemical corrosion behavior variation of WC-10Co4Cr coating subjected to different magnetic treatments and its mechanism

Mechanism for magnetic field induced structural relaxation and accompanying fracture toughness improvement of the thermal spraying coating

Effects Of Wc Crystal Characteristics On Microstructure And Mechanical Property Of Hvof-Sprayed Wc-Cocr Coatings

Magnetic induced re-dissolution and microstructure modifications on mechanical properties of Cr4Mo4V steel subjected to pulsed magnetic treatment

Design for Manufacturing of Cemented Carbide Coated Components Toward High Wear and Impact Resistance Performance

Pulsed Magnetic Treatment of Cobalt for Enhanced Microstructures and Mechanical Properties

Enhanced Tribological Properties of CrN Coatings on Densified Surfaces of Fe-Based Porous Materials Obtained Through Powder Metallurgy and Ultrasonic Shot Peening Treatment

Study on Microstructure and Thermal Fatigue of FeMnCrAl/WC Coatings

Improving the Properties of Magnetic Bearing Shaft Material by HVOF Coating of WC-Metal Powder and Laser Heat Treatment

Promising WC-30WB-10Co Cemented Carbide Coating with Improved Density and Hardness Deposited by High Velocity Oxy-Fuel Spraying: Microstructure and Mechanical Properties

Pulsed Magnetic Field Treatment of WC-TiC-Co Cutting Inserts for Improved Microstructure and Cutting Performance

Effects of WC mass fraction on microstructure and tribological behavior of plasma sprayed FeMnCoCr–WC coatings

Optimizing Wear Resistance and Tensile Strength of Nickel-Based Coatings through Tungsten Carbide Reinforcement

Enhanced Low Cycle Fatigue Properties of Ti-6Al-4V Alloy by Post-treatment Technology of Pulse High-Intensity Magnetic Field

Corrosion and wear resistant WC17Co-TC4 composite coatings with fully dense microstructure enabled by in-situ forging of the large-sized WC17Co particles in cold spray

Comparative tribological study of air plasma sprayed WC–12%Co coating versus conventional hard chromium electrodeposit

Improved fatigue life of SLM-produced TC4 alloy treated by a pulsed magnetic field

Study on Preparation and Wear Resistance of Nicrbsi-Wc/Co Composite Coatings by Pulsed Magnetic Field Assisted Supersonic Plasma Spraying

Research on flame characteristics and coating growth process of titanium alloy in HVAF spraying

Influence of atomic migration mode at different temperatures on the microstructure, mechanical and cavitation erosion behaviors of Co-based alloy coating