PVA-regulated Construction of 3D Rgo-Hosted Na3V2(PO4)2F3 for Fast and Stable Sodium Storage
Shilong Xu,Ying Zhu,Xinyan Li,Yamei Wang,Dong Yan,Xiaobin Niu,Jingxia Jiang,Rui Wu,Jun Song Chen
DOI: https://doi.org/10.1016/j.jechem.2024.07.032
IF: 13.1
2024-01-01
Journal of Energy Chemistry
Abstract:Na3V2(PO4)2F3 3 V 2 (PO 4 ) 2 F 3 (NVPF) is shown to be an attractive cathode material for sodium storage due to its high theoretical capacity and suitable working voltage. However, its low electronic conductivity and poor cycling stability have to be addressed in order for enhanced high-rate performance and cycle life. Herein, we have prepared a 3D reduced graphene oxide (rGO) host-supported NVPF nanocuboids. We discover that polyvinyl alcohol (PVA) serves as an important structural directing agent that bridges between NVPF and rGO through the hydrogen bonding, and thus regulates the formation of the 3D rGO framework with NVPF nanocuboids embedded inside (NVPF@C@rGO). With such a unique construction, NVPF@C@rGO exhibits excellent cycling stability and rate performance for sodium storage, showing high reversible capacities of 121 mAh/g and 113 mAh/g at 1C and 10C, respectively, and 103 mAh/g after 700 cycles at 50C with 98.3% retention. Even at an extremely high current of 100C, it also delivers a reversible capacity of 64 mAh/g, surpassing the performance of many recently reported NVPF-based electrodes. Cyclic voltammetry (CV) and galvanostatic intermittent titration technique (GITT) data confirm the much better kinetic properties of NVPF@C@rGO electrode than the control samples of NVPF@rGO and pure NVPF. In-situ XRD results reveal that the 3D rGO housing can effectively suppress the lattice variation of NVPF, with a maximum volume change of only 1.84% during cycling. Moreover, the in-situ temperature sensing reveals the more stable working temperature of NVPF@C@rGO compared to phase-pure NVPF, suggesting a higher temperature safety of the electrode. Using NVPF@C@rGO as the positive electrode and commercial hard carbon as the negative electrode, a sodium-ion full battery has been assembled with about 110 mAh/g at 1C for 300 cycles, corresponding to an energy density of 291 Wh kg-1 . The construction of 3D rGO housing as a conductive support offers an effective strategy for high-rate, long cycle life and high safety sodium-ion battery cathodes. (c) 2024 Science Press and Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by ELSEVIER B.V. and Science Press. All rights are reserved, including those for text and data mining, AI training, and similar technologies.