Freestanding Na 3 V 2 O 2 (PO 4 ) 2 F/Graphene Aerogels as High-Performance Cathodes of Sodium-Ion Full Batteries
Wei Chang,Xiao-Ying Zhang,Jin Qu,Zhe Chen,Yu-Jiao Zhang,Yanqiu Sui,Xiu-Feng Ma,Zhong-Zhen Yu
DOI: https://doi.org/10.1021/acsami.0c11074
2020-08-19
Abstract:Although sodium vanadium fluorophosphate, Na<sub>3</sub>(VO<sub>1–<i>x</i></sub>PO<sub>4</sub>)<sub>2</sub>F<sub>1+2<i>x</i></sub> (0 ≤ <i>x</i> ≤ 1), is a highly promising cathode candidate for sodium-ion batteries because of its stable structure and high working voltage, the low charge diffusion dynamics and the inactive materials used in traditional coating electrodes reduce the energy density of a sodium-ion full battery. Hence, Na<sub>3</sub>V<sub>2</sub>O<sub>2</sub>(PO<sub>4</sub>)<sub>2</sub>F/graphene aerogels (NVPF/GAs) with a three-dimensional continuous porous network are first prepared by coassembly and freeze-drying. The three-dimensional porous network helps to obtain a high NVPF content of 81 wt %, relieve the volume change for improving the cyclability, and enhance the wettability of the electrode with the electrolyte for accelerating the diffusion dynamics of sodium ions and electrons. As a directly used freestanding cathode without the use of any binder/collector, an optimized freestanding NVPF/GA electrode exhibits excellent cycling and rate performances compared to traditional coating electrodes. The average capacities at current densities of 0.2, 0.5, 1.0, 2.0, and 5.0 C are 135.4, 128.0, 125.1, 121.9, and 115.1 mA h g<sup>–1</sup>, respectively. Especially, it maintains a capacity retention of 100% after 1000 cycles at an ultrahigh current of 40 C. A sodium-ion full battery with the NVPF/GA cathode and the Sb/graphene/carbon anode attains a of 82.1 mA h g<sup>–1</sup> without an obvious decline after 100 cycles.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c11074?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c11074</a>.Zeta potential distribution of NVPF and GO; SEM image of GO; cumulative pore areas and pore size distributions of NVPF/GA hybrids; EDX mapping images of NVPF; XPS spectra of NVPF/GA hybrids; charge/discharge and CV curves of the freestanding NVPF/GA 400 electrode; CV curves of different electrodes; CV peak current versus the square root of scan rate; EIS impedance of different electrodes; structural characterization of the freestanding NVPF/GA 400 electrode after long cycling; characterization of Sb/G/C composite; rate performances of a sodium-ion full cell; and comparison of electrochemical performances (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c11074/suppl_file/am0c11074_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology