Dually Decorated Na 3 V 2 (PO 4 ) 2 F 3 by Carbon and 3D Graphene as Cathode Material for Sodium‐Ion Batteries with High Energy and Power Densities

Lizhen Hu,Siqi Cheng,Shunhua Xiao,Wenna Li,Zhuo Chen,Wei Li,Bin Huang,Qingquan Liu,Quanqi Chen

DOI: https://doi.org/10.1002/celc.202000881

IF: 4

2020-09-09

ChemElectroChem

Abstract:The dually decorated Na 3 V 2 (PO 4 ) 2 F 3 by in‐situ formed carbon and three‐dimensional graphene (NVPF/C@3DG) is prepared via two hydrothermal steps and a high‐temperature calcination. Benefiting from the high electronic conductivity of carbon and 3DG, high surface area and the resulted high diffusion coefficients of Na + , NVPF/C@3DG displays superior electrochemical performance to the control NVPF/C. Between 2.5 and 4.5 V (vs. Na + /Na), NVPF/C@3DG presents the initial discharge capacity of 123.6 mAh g ‐1 at 0.2C (25.6 mA g ‐1 ) and capacity retention of 92.1% after 60 cycles, while NVPF/C shows initial discharge capacity of 119 mAh g ‐1 and capacity retention of 84.1% under the identical test conditions. Even at 15C, the initial discharge capacity and capacity retention after 1000 cycles of NVPF/C@3DG are as high as 91.2 mAh g ‐1 and 82.9%, respectively, much better than the initial discharge capacity of 71.2 mAh g ‐1 and the corresponding capacity retention of 76.4% for NVPF/C, respectively.

electrochemistry