Abstract:(SiC+TiB 2 )/AlSi10Mg composite powders with 5 wt% micro-SiC particles and 1.5 wt% nano-TiB 2 particles were prepared by high energy ball milling, and hybrid particle reinforced aluminum matrix composites (AMCs) were fabricated by SLM. This study systematically investigated the effects of SiC and TiB 2 particles on the phase composition, microstructure evolution, grain crystallization, and mechanical properties. The machanisms of potential strengthening and fracture mechanisms were revealed. The tribological behaviors of the hybrid particle reinforced AlSi10Mg composites under different friction conditions were explored as well. The results show that the 1.5 wt% nano-TiB 2 particles provided sufficient nucleation sites for grain growth, completely transforming from coarse columnar to fined equiaxed grains. The average grain size decreases from 7.98 μm to 3.34 μm, and the texture is significantly weakened, which is beneficial to the homogenization of the microstructure, thereby improving the mechanical properties of the SiC/AlSi10Mg composites. The (SiC+TiB 2 )/AlSi10Mg composites showed a high ultimate tensile strength (∼ 489.1 MP), hardness (172.2 HV) and elongation of 8.2 %. The enhancement of mechanical properties was attributed to Orowan strengthening, fine grain strengthening, and load-bearing strengthening. Due to the Si precipitates and fine microstructure, a low wear rate of 0.50 × 10 −5 g/m was obtained, 10.7 % lower than that of SLM formed SiC/AlSi10Mg composites. The friction process is affected by abrasive wear, adhesive wear and delamination wear. It is aspired that the current approach can provide guidance for the design of new alloy systems with excellent performance.

Preparation and Characterization of Al-Mg-Si Matrix Composites Reinforced with Ti2(Al,Si)C Solid Solution

Preparation and characterization of Al-Mg-Si matrix composites reinforced with Ti 2 (Al,Si)C solid solution

In Situal3ti–al2o3 Intermetallic Matrix Composite: Synthesis, Microstructure, and Compressive Behavior

Microstructure characterization and mechanical properties of in situ synthesized Ti2(Al,Si)C reinforced Al composites

Preparation, Microstructure and Mechanical Properties of In-Situ TiC/Al–Si–Fe Aluminum Matrix Composites

Microstructure and Mechanical Properties of Ti2AlC Particle and In-Situ TiAl3 Reinforced Pure Al Composites

Microstructure, mechanical properties and strengthening mechanisms of in-situ prepared (Ti5Si3 + TiC0.67)/TC4 composites

Preparation and Characterization of In Situ (TiC-TiB2)/Al-Cu-Mg-Si Composites with High Strength and Wear Resistance

Microstructure, solidification behavior and mechanical properties of Al-Si-Mg-Ti/TiC fabricated by selective laser melting

In-situ synthesized a dual-scale Ti 2 AlC reinforced TiAl composites with superior mechanical properties

Processing, Microstructure and Mechanical Properties of Ti6Al4V Particles-Reinforced Mg Matrix Composites

In-situ TiC/Ti composites based on Ti 2 AlC–Ti system: Reaction process, microstructure, and mechanical properties

Microstructure and Mechanical Properties of Ti2AlC-reinforced TiAl Composites

Preparation of in situ TiC@TiN core–shell and Ti2N–Al4C3 nanoparticles and their effects on Al–Zn–Mg–Cu alloy

Investigation on microstructure and properties of TiC0.5-Al2O3/Cu composites fabricated by a novel in-situ reactive synthesis

Achieving high combination of strength and ductility of Al matrix composite via in-situ formed Ti-Al3Ti core-shell particle

Preparation and toughness mechanism of in-situ Ti<sub>3</sub>AlC<sub>2</sub> enhanced and toughened TiAl<sub>3</sub> matrix composites

Microstructure and Properties of TiC/AlMgSc Composites by Selective Laser Melting

Fabrication and characterization of in-situ TiAl matrix composite with controlled microlaminated architecture based on SiC/Al and Ti system

Fabrication, microstructure and mechanical properties of TiAl matrix composite reinforced by submicro/nano-Ti 2 AlC

Microstructure evolution and mechanical properties of selective laser melting fabricated hybrid particle reinforced AlSi10Mg composites