Abstract:To improve the ductility of particulate reinforced metal matrix composite, an A356 aluminum alloy based composite reinforced with in-situ spheroidal core-shell structured (CS) particulates was fabricated via powder thixoforming. The generated CS particulates have a uniform two-layered annular intermetallic shell surrounding a Ti core, which renders the composite an excellent elongation of 12% equivalent to that of the A356 alloy, while maintaining a high strength. Subsequent solution treatment at 530 °C for 3 h further improve its ultimate tensile strength, yield strength and elongation from 230 MPa, 138 MPa and 12% to 243 MPa, 168 MPa and 17%, respectively, i.e., the strength and ductility are simultaneously improved. The microstructure evolution, particularly the evolution of the CS particulates during solution treatment, the resulted mechanical properties and corresponding strengthening as well as toughening mechanism were comprehensively discussed. A modified shear lag model established by introducing an equivalent coefficient into the particulate fraction aimed at the CS particulates and taking the strengthening role of eutectics into account can reasonably describe the strengthening mechanisms and accurately predict the yield strength of the composite during solution treatment. But the achieved toughening model through simplifying both the particulates and eutectic into equivalent monolithic particulates can only accurately calculate the changing tendency of ductility with the solution time and partially depict the toughening mechanisms, which should be further clarified in future.

Achieving high combination of strength and ductility of Al matrix composite via in-situ formed Ti-Al3Ti core-shell particle

In Situal3ti–al2o3 Intermetallic Matrix Composite: Synthesis, Microstructure, and Compressive Behavior

MMCs with Controlled Non-Uniform Distribution of Submicrometre Al2O3particles in 6061 Aluminium Alloy Matrix

Preparation of in situ TiC@TiN core–shell and Ti2N–Al4C3 nanoparticles and their effects on Al–Zn–Mg–Cu alloy

Fabrication, microstructure and mechanical properties of TiAl matrix composite reinforced by submicro/nano-Ti 2 AlC

Enhancing strength-ductility synergy in nano-sized TiB 2 /Al composite via rapid solidification and thermo-mechanical processing

A novel core-shell TiCx particle by modifying TiCx with B element and the preparation of the (TiCx + AlN)/Al composite

Simultaneously strengthening and toughening a core-shell structured particulate reinforced aluminum alloy-based composite by solid solution treatment

Fabrication and strengthening mechanism of dual-phased and bimodal-sized (Si3N4p + TiB2p)/6061Al hybrid composite

In-situ synthesized a dual-scale Ti 2 AlC reinforced TiAl composites with superior mechanical properties

Enhanced mechanical properties of a novel heat resistant Al-based composite reinforced by the combination of nano-aluminides and submicron TiN particles

In-situ synthesis of Al2O3-reinforced high Nb–TiAl laminated composite with an enhanced strength-toughness performance

Preparation and characterization of Al-Mg-Si matrix composites reinforced with Ti 2 (Al,Si)C solid solution

Interfacial/intragranular reinforcement of titanium-matrix composites produced by a novel process involving core-shell structured powder

Preparation and toughness mechanism of in-situ Ti3AlC2 enhanced and toughened TiAl3 matrix composites

Strengthening behavior of B doped TiC particles on an Al–Zn–Mg alloy

Revealing the formation, strengthening and toughening mechanism of a new (Ti3AlC2+Al2O3)p /Al3Ti composite with strength-ductility synergy

Simultaneous Improvement in Strength and Ductility of TC4 Matrix Composites Reinforced with Ti1400 Alloy and In Situ-Synthesized TiC

Hierarchically heterogeneous strategy for Ti 2 AlC/TiAl composite with superior mechanical properties

Preparation, Microstructure and Mechanical Properties of In-Situ TiC/Al–Si–Fe Aluminum Matrix Composites

Balancing the strength and ductility of Ti2AlC/TiAl composite with a bioinspired micro-nano laminated architecture