Abstract:Highlights • C/C-HfC-SiC sharp leading edges were prepared in near-net shape via precursor infiltration and pyrolysis. • The preferred sample possessed almost zero degradation at a temperature up to 2371 °C for 120 s. • The sharp leading edge with less SiC exhibited a remarkably low linear recession rate above 2500 °C. • The superior ablation resistance is attributed to the thermally stable oxide scale with oxygen barrier ability. HfC-SiC-modified carbon/carbon composite (C/C-HfC-SiC) sharp leading edges (SLEs) were prepared via precursor infiltration and pyrolysis for potential hypersonic applications. The effect of SiC proportion on the ablation behavior of the SLEs under oxyacetylene flames with 2.38 MW/m 2 and 4.18 MW/m 2 was investigated. The preferred sample with a volume ratio of HfC to SiC of 0.74 possessed almost zero degradation (linear recession rate 0.6 μm/s) up to a temperature of 2371 °C. As the temperature increases to 2527 °C in the latter condition, the SLE with less SiC (the volume ratio of HfC to SiC is 1.10) exhibited a linear recession rate of 1.03 μm/s during cyclic ablation of 3 × 40 s. Relatively more SiC addition is favorable under lower heat flux due to the better oxygen barrier performance of the scale. However, superior ablation resistance is available under higher heat flux with less SiC addition due to the higher thermal stability of the resulting oxide scale. Graphical abstract Download : Download high-res image (259KB) Download : Download full-size image

Ablation Behaviour of C/C-HfC-SiC Composites Prepared by Joint Route of Precursor Infiltration and Pyrolysis and Gaseous Silicon Infiltration

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Comparative ablation behaviors of C/SiC–ZrC and C/SiC–HfC composites prepared by ceramization of carbon aerogel preforms

Cyclic ablation behavior of mullite-modified C/C-HfC-SiC composites under an oxyacetylene flame at about 2400 °C

Preparation and Properties of C/SiC Composites Reinforced by High Thermal Conductivity Graphite Films

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

C/C-HfC-SiC composites with simultaneous the resistance to ultra-high temperature airflow erosion and high temperature oxidation

Ablation behavior of 3D PyC-Cf/SiHfBOC Composites under an oxyacetylene torch environment above 2000 °C

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Investigation on the oxidation and ablation behaviors of HfB2-SiC-Si/SiC-Si coatings for carbon/carbon composites

Superior ablation resistance of C/C-HfC-SiC composite sharp leading edges above 2500 °C prepared by precursor infiltration and pyrolysis

Ablation performance of C/C-ZrC-SiC composites with in-situ YSi 2 -doped ZrC-SiC-ZrSi 2 coating under oxyacetylene torch

Ablation behavior of mullite modified C/C-SiC-HfC composites under oxyacetylene torch for single and cyclic ablations with two heat fluxes

Microstructure and ablation resistance of C/C-HfC-SiC composites prepared by RMI with different powder particle sizes

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Cyclic ablation behavior of C/C–ZrC–SiC composites under oxyacetylene torch

Ablation of advanced C/C-ZrC-SiC leading edge composites

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

Ablation behaviour of Csf/ZrB2-SiC composites fabricated by direct ink writing and reactive melt infiltration

Ablation behavior of thin-blade co-deposited C/Cx-SiCy composites under the influence of the complex fluid conditions of the oxyacetylene torch