Abstract:We report on erbium (Er) related electroluminescence (EL) in the visible and near infrared (NIR) regions from the light-emitting device (LED) based on the Er-doped ZnO (ZnO:Er)/n-Si isotype heterostructure formed by sputtering ZnO:Er film on n-Si/n(+)-Si epitaxial wafer. Herein, the ZnO:Er film exhibits n-type in electrical conduction. The aforementioned LED is electroluminescent only under sufficiently high forward bias with the negative voltage connecting to n(+)-Si substrate. Such forward bias enables the electrons from n-Si to enter into the ultra-thin SiOx (x <= 2) layer inherently existing between the ZnO:Er film and n-Si via Poole-Frenkel conduction mechanism and, subsequently, to drift into the ZnO:Er film thus becoming hot electrons, which impact-excite the Er3+ ions to emit characteristic visible and NIR light. Furthermore, the Er-related EL from the aforementioned LED can be significantly enhanced through adopting the strategy of co-doping F ions into the ZnO host, which brings about twofold primary effects. Firstly, due to the atomic size compensation between F and Er3+ ions, the ZnO crystal grains become larger to accommodate much more optically active Er3+ ions. Secondly, the partial substitution of F ions for O2- ions around the Er3+ ion reduces the symmetry of pseudo-octahedral crystal field of Er3+ ion, thus increasing the probabilities of intra-4f transitions of Er3+ ions. We believe that this work sheds light on developing efficient silicon-based LEDs using the Er-doped oxide semiconductors. (C) 2019 Optical Society of America under the terms of the OSA Open Access Publishing Agreement

Highly Efficient Electroluminescence from SnO2 Nanocrystals and Er3+ Co-Doped Silica Thin Film Via Introducing Ca2.

Enhanced Electroluminescence from SnO2 Nanocrystals/er3+ Co-Doped Silica Thin Film Via Yb3+ Doping

Near-infrared Light Emitting Devices from Er Doped Silica Thin Films Via Introducing SnO2 Nanocrystals

Enhanced electroluminescence from SnO_2 nanocrystals/Er^3+ co-doped silica thin film via Yb^3+ doping

Highly efficient near-infrared emission in Er3+ doped silica films containing size-tunable SnO2 nanocrystals.

Low Driving Voltage and High Reliability 1.54 Μm Electroluminescence from SnO2:Er/p-Si Heterostructured Devices Via Energy Transfer Effect

Alkaline Earth Metal Ion Doping to Enhance the Light Emission from Er3+:SnO2 Nanocrystal Co-doped Silica Films

Alkaline Earth Metal Ions Doping to Enhance the Light Emission from Er3+: SnO2 Nanocrystals Co-doped Silica Films

Electroluminescence from Metal–oxide–semiconductor Devices Based on Erbium Silicate Nanocrystals and Silicon Nanocrystals Co-Embedded in Silicon Oxide Thin Films

Improved Resonant Energy Transfer and Light Emission from SnO2 Nanocrystals and Er3+ Embedded in Silica Films Via Yb3+ Co-Doping

Photoluminescence from Er 3 + Ion and SnO 2 Nanocrystal Co-Doped Silica Thin Films

Improved Sensitization Efficiency in Er(3+) Ions and SnO2 Nanocrystals Co-Doped Silica Thin Films.

Confinement Effect and Low-Defect Density-Induced Long Lifetime Er Silicate Nanowire Embedded in Silicon Oxide Film.

Enhanced Electroluminescence From Sn/Er Co-Doped SiO 2 Thin Film by Controlling Sn Content

Electroluminescence from Light-Emitting Devices Based on Erbium-Doped ZnO/n-Si Heterostructures: Enhancement Effect of Fluorine Co-Doping

Enhanced Luminescence of Erbium Doped Ga2O3 Films and Devices by Optimizing Annealing Process

Enhanced Electroluminescence From Sn/E Co-Doped SiO<sub>2</sub> Thin Film by Controlling Sn Content

Efficient Sensitized Photoluminescence from Erbium Chloride Silicate Via Interparticle Energy Transfer

Efficient Sensitized Photoluminescence of Er Silicate in Silicon Oxide Films Embedded with Amorphous Silicon Clusters, Part II: Photoluminescence

Effects of Excess Silicon on the 1540 Nm Er3+ Luminescence in Silicon Rich Oxynitride Films

Strong Energy-Transfer-Induced Enhancement of Er3+ Luminescence in In2o3 Nanocrystal Codoped Silica Films