Abstract:In this study, a high-performance Mg–8Gd–2Y–1Zn–6Li (wt%) alloy having a TYS of 202 ± 2.6 MPa, UTS of 243 ± 2.1 MPa and EL of 10.7 ± 2.3% was successfully fabricated by casting, heat treatment and hot extrusion. The effects of intermetallic compounds on microstructure and mechanical properties were deeply investigated. The results show that the studied alloy consists of coarse deformed α-Mg grains with (0001) basal texture, fine recrystallized β-Li grains with (002) texture and three Mg3RE phase variants, which are bulk Mg3RE phase with a size range of 10–30 µm, spot Mg3RE phase with a size range of 1–2 µm and spherical Mg3RE phase with a size range of 0.3–1 µm, respectively. The spherical Mg3RE phase has a strong dispersion strengthening effect, while the bulk Mg3RE phase acts as crack resources and deteriorates the ductility. A novel island-like <math>β1R</math> phase (FCC, a = 0.78 nm) is found for the first time in the Mg-Gd-Li based alloys. It has a coherent <math>(1̅12)β1R</math>//<math>(101̅0)α</math> interface at the broad facet and a semi-coherent <math>(1̅11)β1R</math>//<math>(112̅0)α</math> interface at the end facet. The <math>β1R</math> phase transforms from <math>βH</math> phase at the semi-coherent interface by atomic shear of RE and Mg atoms. The <math>β1R</math> phase provides a significant precipitation strengthening effect to the studied alloy, while the dissolution of <math>β1R</math> phase results in the age-softening phenomenon. The high-performance of the studied alloy is mainly attributed to the α/β duplex structure, three Mg3RE phase variants, and <math>β1R</math> phase.

Microstructure and Mechanical Properties of a Cast Heat-Resistant Rare-Earth Magnesium Alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Effects of solid solution and aging process on microstructure and mechanical properties of Mg-Gd-Y alloy

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Strengthening of Mg Alloy with Multiple RE Elements with Ag and Zn Doping via Heat Treatment

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Development of high mechanical properties and moderate thermal conductivity cast Mg alloy with multiple RE via heat treatment

The Research of Microstructure and Mechanical Properties of Mg–7Gd–3Y–1Nd–0.5Zn–0.5Zr (wt%) Alloy

Microstructure and Mechanical Properties of As-Cast and Heat Treated Mg-15Gd-3Y Alloy

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy

Influence of Heat Treatment and Hot Extrusion on the Microstructure and Tensile Properties of Rare Earth Modified Mg-Zn Based Alloy

Microstructural Evolution and Mechanical Properties of Mg-5y-5gd-Xnd-0.5zr Magnesium Alloys at Different States

Microstructure Characterization and Mechanical Properties of a Zn and Rare Earth Modified Mg Alloy

Microstructures and mechanical properties of as-extruded Mg–8Gd–2Y–1Zn–6Li alloy

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-1Zn-0.5Zr Alloy

Study on Microstructure and Strengthening Sources of As-Cast Mg-Zn-RE-Zr Alloy during Heat Treatments

Study on Tensile Behavior at Various Temperatures of the Mg-7Gd-5Y-1Nd-2Zn-0.5Zr Alloy

Microstructure Evolution and Mechanical Properties of Mg-7Gd-3Y-1Nd-2Zn-0.5Zr Alloy During Two-Step Homogenization Heat Treatment

Microstructure Evolution Mechanism and Mechanical Properties of Mg-RE Alloy at a Critical Transition Temperature of Material Performance

Effect of heat treatment on microstructure and mechanical properties of Mg-4Y-1.6Nd-1Sm-0.5Zr alloy

High Strength Extruded Mg–5Zn–2Nd–1.5Y–0.6Zr–0.4Ca Alloy Produced by Electromagnetic Casting