Structure of Al-modified Silicide Coating on an Nb-silicide-based Ultrahigh Temperature Alloy Prepared by Pack Cementation Technique

Xuhong Guo

2007-01-01

Abstract:Al-modified silicide coatings on an Nb-silicide-based ultrahigh temperature alloy were prepared by either a two-stage pack cementation process or a co-deposition pack cementation process respectively.The two-stage process coating was firstly pack siliconized at 1150℃/4h and then pack aluminized at 800~1000℃ for 4h.It has been found that the main constituent phase of the pack siliconized coating was(Nb,X)Si2(X represents Ti,Cr and Hf).Small(Nb,Ti)3Si5Al2 particles were found to exist in the(Nb,X)Si2 layer when the aluminizing temperature reached at 860℃,and a(Nb,Ti)(Al,Si)3 layer formed between the pack siliconized layers and the matrix when the aluminizing temperature reached above 900℃.The coating prepared by co-depositing Si-Al at 1050℃/20h had a multiple layer structure: the outer layer was composed of(Nb,Ti)3Si5Al2 and(Nb,Ti)(Al,Si)3,and the middle layer was composed of(Nb,X)Si2 in the upper part and(Nb,X)5Si3 in the lower part,and the inner layer was composed of(Nb,Ti)Al3 and(Cr,Al)2(Nb,Ti).