Abstract:In this work, the following coatings were obtained by magnetron sputtering of (MoTaNbZrHf)SiB and SiBC targets: single-layer (MoTaNbZrHf)SiB, double- and multilayer (MoTaNbZrHf)SiB/SiBC, and nanocomposite (MoTaNbZrHf)-Si-BC coatings. Particular attention was paid to studying the effect of increased silicon content on the structure and oxidation resistance of developed coatings. Results showed that single-layer and nanocomposite coatings have a homogeneous structure with a uniform distribution of elements across the thickness. Double- and multilayer coatings contained (MoTaNbZrHf)-Si-B/Si-B-C layers with a thickness of 9.1/3.9 and 1.7/0.6 μm, respectively. Introduction of additional silicon-containing phases into the composition of (MoTaNbZrHf)-Si-B coatings led to a decrease in the specific mass change from –3.1 to 0.15–0.20 mg/cm 2 at a temperature of 1000°C. Annealing at a temperature of 1500°C showed that the double-layer (MoTaNbZrHf)-Si-B/Si-B-C coatings have a minimum oxide layer thickness of 9.2 μm and a specific mass loss of 0.95 mg/cm 2 , which is 1.5 and 1.8 times lower than the values obtained for the single-layer (MoTaNbZrHf)-Si-B coating. At 1600°C, the single-layer (MoTaNbZrHf)-Si-B coating was completely oxidized, while the double- and multilayer (MoTaNbZrHf)-Si-B/Si-B-C coatings were partially preserved, which is due to the high silicon content in their composition.

Design and preparation of MoSi2/SiO2-Nb2O5/NbSi2 multilayer coating on Nb alloy: Microstructure and hot corrosion behavior

Formation and Oxidation Behavior of Mo-Si-B Composite Coatings with B-rich Interlayer Prepared by Slurry Sintering Method

ZrSi2/SiO2-Nb2O5/NbSi2 multi-layer coating formed on niobium alloy by HAPC combined with LPDS: Microstructure evolution and high temperature oxidation behavior

Enhanced high-temperature oxidation resistance of HfSi 2 -modified silicon based multilayer ceramic coating on Nb alloy prepared by a novel strategy

Formation and oxidation behavior of Ce-modified MoSi2-NbSi2 coating on niobium alloy

Microstructural Characterization and Anti‐Oxidation Properties of Molybdenum Disilicide Coating on Niobium by Spent MoSi 2 ‐Based Materials

Development and oxidation behavior of high entropy silicide (NbMoTaWV)Si2 coatings on NbMoTaWV alloy

Microstructure and oxidation resistant of Si–NbSi2 coating on Nb substrate at 800°C and 1000°C

Preparation, properties and high-temperature oxidation resistance of MoSi2-HfO2 composite coating to protect niobium using spent MoSi2-based materials

Study on the Oxidation Behavior of TiB2-CeO2-Modified (Nb,Mo,Cr,W)Si2 Coating on the Surface of Niobium Alloy

Preparation of a dense MoSi2 coating on Nb Si based alloy with enhanced oxidation resistance via slurry sintering method

Preparation and high‐temperature oxidation resistance of multilayer MoSi 2 /MoB coating by spent MoSi 2 ‐based materials

A novel composite Si-Mo-Ti coating with Ti concentration gradient for Nb-Si based ultrahigh temperature alloy prepared by slurry sintering

Recycling of MoSi2-based industrial solid wastes for the fabrication and high-temperature oxidation behavior of MoSi2–ZrSi2–SiC composite coating

Formation and oxidation behavior of refractory high-entropy silicide (NbMoTaW)Si2 coating

Morphology and Structure of Mo(Si,Al)_2 High Temperature Oxidation Resistant Coating

Oxidation-Resistant Coatings Based on High-Entropy Alloy (MoTaNbZrHf)SiB with Increased Silicon Content, Deposited by Magnetron Sputtering

Influence of Ta2O5 on the micromorphology and high-temperature oxidation resistance of MoSi2-based composite coating for protecting niobium

Microstructure and high-temperature oxidation resistance of MoSi2-ZrO2 composite coatings for Niobium substrate

High-temperature oxidation resistance and high emissivity of a novel NbSi2/SiO2-Nb2O5/MoSi2-Yb2O3 multilayer coating on Nb substrate for thermal protection

Multi-functional superhydrophobic coatings on mg Li alloys via SiO 2 nano particles assembled surface modification