Abstract:The dispersoid precipitation behavior during the solutionizing and aging of Al-xwt.%Cu-1.0 wt.% Mn alloys (x = 2.0, 4.5, and 7.5) and contribution to mechanical properties were investigated using tensile testing and microstructural characterization. A shell-core structure of primary α-Al dendrites is found in Al-Cu-Mn alloys, in which the Cu content in the shell is higher than that in the core. The area of shell zone (Cu-rich) increases with an increase in Cu content in the alloy. Large amounts of fine dispersoid Al-Cu-Mn particles precipitate in solution. An alloy with low Cu content results in only the TMn (Al20Cu2Mn3) particles being precipitated. However, in an alloy with high Cu content, AlCu3Mn2 particles are first found to precipitate beside TMn. However, this precipitation behavior is uneven. The precipitation zones in the solution microstructure are consistent with the Cu-rich regions in the as-cast microstructure. A number of fine particles (dozens nanometer in size) are first found to precipitate on the rod-like TMn particles during the aging phase. The redissolution and granulation of the eutectic CuAl2 phase during the solutionizing process result in the formation of particle-free bands between the precipitation zones. The tension test at 300°C demonstrates that the increase in high temperature strength is due to the dispersoid precipitation during solutionizing, and the precipitation behavior in the aging phase has little or no effect, however, largely improves the tensile strength at room temperature. High temperature strength is significantly increased with an increase in Cu content, which correlates to an increase in number and decrease in size of TMn and AlCu3Mn2 particles.

Effect of Ti2Cu Precipitates on Mechanical Behavior of Ti–2.5Cu Alloy Subjected to Different Heat Treatments

Precipitation Behavior and Mechanical Properties of a Novel Cu–2Fe-0.5Ti Alloy Produced by Thermos-Mechanical Treatment

Mechanical Behavior and Deformation Mechanisms of Ti–2.5Cu Alloy Reinforced by Nano-Scale Precipitates at 293 and 77 K

Evolutions of the Microstructures and Mechanical Properties of Ti-2.8 Wt%cu Alloy During Heat Treatment

Influence of Ti Elements on the Evolution of Microstructure, Mechanical Properties and Thermal Stability of Al-Cu Alloy

Effects of Cooling Rate and TiC Nanoparticles on the Microstructure and Tensile Properties of an Al–Cu Cast Alloy

Crystallography and diffraction patterns of the precipitates in Cu-3 wt% Ti alloy

Effect of TiC Nano-Particles on the Mechanical Properties of an Al-5Cu Alloy after Various Heat Treatments

Effect of micro-alloying element Ti on mechanical properties of Cu–Cr alloy

Characterization on the Precipitates in the Ti-Ni-Al-Zr Alloy During Heat Treatment

Precipitation Behavior and Performance Evolution of Cold-Rolled Cu-Ti-fe Alloy During Heat Treatment

Effect of temperature on mechanical behavior of Cu–Cr–Co–Ti alloys

Effect of precipitation phase morphology on mechanical properties of Ni-Ti shape memory alloy

Microstructure Evolution and Nano-Precipitate of Multi-Stage Heat-Treated Ti–45Al–2Nb–2Cr-0.3C Alloy

Influence of Ti2Cu Precipitates on B19 Martensite Structure in a Ti-rich Ti–Ni–Cu Thin Film

Heterogeneous Precipitate Microstructure Design in Β-Ti Alloys by Regulating the Cooling Rate

Investigation of the mechanical properties of TiC particle-reinforced Al-Cu alloys: insights into interface precipitation mechanisms and strengthening effects

Effects of Ti and Cu on the Microstructure Evolution of AlCoCrFeNi High-Entropy Alloy During Heat Treatment

Effect of Heat Treatment on Morphology Evolution of Ti2Ni Phase in Ti-Ni-Al-Zr Alloy

Effect of Cu on Nanoscale Precipitation Evolution and Mechanical Properties of a Fe-NiAl Alloy.

Uneven Precipitation Behavior During the Solutionizing Course of Al-Cu-Mn Alloys and Their Contribution to High Temperature Strength