Abstract:Ferromagnetic Fe3O4 nanoparticles were synthesized and then self-assembled into microparticles via a solvothermal method, using FeCl3-6H(2)O as the iron source, sodium oleate as the surfactant, and ethylene glycol as the reducing agent and solvent. The obtained Fe3O4 microparticles were characterized by X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy and vibrating sample magnetometer (VSM). The size and morphology of the particles were examined using transmission electron microscopy (TEM) and scanning electron microscopy (SEM). The Fe3O4 microparticles of nearly monodisperse diameters, controllable in the range of 120-400 nm, consist of assemblies of Fe3O4 nanoparticles with a diameter of 22 nm. The effects of reaction time, amount of surfactant and NaAc on the products were discussed. Interestingly, by using the pre-synthesized Fe3O4 microparticles as the growth substrates, spherical and smooth-looking Fe3O4 microparticles with average diameter of 1 mu m were obtained. A plausible formation process was discussed. (C) 2011 Chinese Society of Particuology and Institute of Process Engineering, Chinese Academy of Sciences. Published by Elsevier B.V. All rights reserved.

Solvothermal synthesis and characterization of size-controlled monodisperse Fe 3 O 4 nanoparticles

Solvothermal synthesis and characterization of size-controlled monodisperse Fe<sub>3</sub>O<sub>4</sub> nanoparticles

Solvothermal synthesis and characterization of size-controlled monodisperse Fe 3 O 4</s

Synthesis of Monodispersed Fe3O4 Magnetite Nanoparticles by ethylene glycol solvothermal method

Solvothermal Synthesis and Characterization of Size-Controlled Fe3o4 Nanoparticles

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Large-scale synthesis and characterization of monodisperse Fe3O4 nanocrystals

Controlled Synthesis And Characterization Of Monodisperse Fe3o4 Nanoparticles

Controlled Synthesis and Characterization of MonodisperseFe<sub>3</sub>O<sub>4</sub>Nanoparticles

Size Controllable Synthesis of Magnetite Fe3O4 Nanoparticles

A simple solvothermal synthesis and characterization of round-biscuit-like Fe3O4 nanoparticles with adjustable sizes

Solvothermal Synthesis of Magnetic Fe3o4 Microparticles Via Self-Assembly of Fe3o4 Nanoparticles

Synthesis and Characterization of Monodisperse Fe3O4Nanospheres with Uniform Particle Size Distribution by a Simple Solvothermal Method

Solvothermal Synthesis and Properties of Monodisperse Magnetite Nanoparticles

Solvothermal synthesis and characterization of NiFe2O4 nanospheres with adjustable sizes

Shape-Controlled Synthesis and Magnetic Properties of Monodisperse Fe3o4 Nanocubes

Preparation and Surface Modification of Monodisperse Fe3O4 Nanoparticles

Synthesis and Characterization of Fe3O4 Nanoparticles by a Solvothermal Method

Synthesis of Highly Dispersed Fe3O4 Submicrometer Spheres in a One-Pot Anion-induced Solvothermal System

Magnetic Monodisperse Fe3o4 Nanoparticles

Controllable Synthesis and Magnetic Properties of Monodisperse Fe3o4 Nanoparticles