Abstract:In this study, the formation processes of TiC in a Cu–Ti–SiC system following the addition of a Ti–SiC mixture into a Cu melt were studied by analyzing the reaction intermediates, and the influence of the synthesis processes on the TiC microstructure was examined. It is found that, upon the addition of Ti–SiC into the Cu melt, the reaction of Ti and Cu to form a Cu–Ti liquid phase occurred first, followed by the reaction between liquid Ti, denoted as Ti(l), and SiC. However, the Ti(l)–SiC reaction processes vary depending on the reaction conditions and significantly influence the microstructures of the TiC particles, especially their dispersion in the Cu matrix. Under certain conditions, such as a lower reaction temperature and larger SiC size, SiC does not directly react with Ti(l). It first transforms into graphite through the outward diffusion of Si; subsequently, the graphite phase reacts with Ti(l) to form TiC. In this case, the synthesized TiC particles tend to connect with each other to form agglomerates. Under conditions conducive to the direct reaction of the Ti(l)–SiC system, such as a higher reaction temperature and smaller SiC size, Ti(l) and SiC first react to form a Ti3SiC2 phase that then decomposes into TiCx and Ti–Si phases and eventually transforms into TiCy (x > y) and amorphous or crystalline Si. In this case, the formed Ti–Si or Si phase can prevent the agglomeration of TiC particles, leading to their more uniform distribution in the prepared Cu matrix composite.

Phase Evolution and Reaction Mechanism During Synthesis of Ti3SiC2 from Ti-Si-C and Ti-SiC-C Systems

Synthesis of Ti3SiC2 from powder blend of Ti, Si and TiC

Phase reaction and diffusion path of the SiC/Ti system

Phase stability of SiC against Ti at high temperature

Reaction Mechanism of Ti<SUB>3</SUB>SiC<SUB>2</SUB> Formed on the Diamond

Phase stability of Ti3SiC2 at high pressure and high temperature

Ti3sic2 Powder Synthesis from Ti/Si/Tic Powder Mixtures

Low Temperature and Pressureless Synthesis of High-Purity Ti3SiC2 MAX Phase from TiC Via Κ-Al2o3 Addition Through Reactive Melt Infiltration

Reaction mechanism of Ti3SiC2 formed on the diamond

Synthesis and Some Properties of Ti3SiC2by Hot Pressing of Titanium, Silicon, and Carbon Powders Part 1 – Effect of Starting Composition on Formation of Ti3SiC2and Observation of Ti3SiC2crystal Morphology

Reaction mechanism and kinetics in Ti3SiC2 synthesised from oxides

Synthesis of single-phase Ti3SiC2 with the assistance of liquid phase formation

Reaction Synthesis of Ti3SiC2 from Mixture of Elemental Powders

Formation Mechanism of Titanium Silicon Carbide: the Effect of Different Composition of Starting Materials

Influence on TiC microstructure from different synthesis processes in the Cu–Ti–SiC system

Experimental and thermodynamic investigations in the Ti‐Si‐C system

Synthesis of Single-Phase Ti3SiC2 Powder

Synthesis of Ti3SiC2 powder from 1Ti/(1+x)Si/2TiC powder mixtures

Evolution Process of the Synthesis of TiC in the Cu–Ti–C System

Ti3SiC2 Powder Synthesis

Effects of SiC Amount on Phase Compositions and Properties of Ti 3 SiC 2 -Based Composites