NaNbO₃-based short-range antiferroelectric ceramics with ultrahigh energy storage performance

Lan Zhang,Zhengu Chen,Gengguang Luo,Fanrong Ai,Nengneng Luo

DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.07.002

IF: 5.7

2023-01-01

Journal of the European Ceramic Society

Abstract:Lead-free NaNbO3 (NN) antiferroelectric ceramics provide superior energy storage performance and good temperature/ frequency stability, which are solid candidates for dielectric capacitors in high power/pulse electronic power systems. However, their conversion of the antiferroelectric P phase to the ferroelectric Q phase at room temperature is always accompanied with large remnant polarization (Pr), which significantly reduces their effective energy storage density and efficiency. In this study, to optimize the energy storage properties, shortrange antiferroelectric (0.95-x)NaNbO3-xBi(Mg2/3Nb1/3)O-3-0.05CaZrO(3) (xBMN) ceramics were designed to stabilize the antiferroelectric phase, in which the local random fields were simultaneously constructed. The results showed that the antiferroelectric orthorhombic P phase was transformed into the R phase, and the local short-range random fields were generated, which effectively inhibited the hysteresis loss and Pr. Of great interest is that the 0.12BMN ceramics displayed a large recoverable energy storage density (Wrec) of 5.9 J/cm(3) and high efficiency (eta) of 85% at the breakdown strength (Eb) of 640 kV/cm. The material also showed good frequency stability in the frequency range of 2-300 Hz, excellent temperature stability in the temperature range of 20-110., and a very short discharge time (t0.9 similar to 4.92 mu s). These results indicate that xBMN ceramics have great potential for advanced energy storage capacitor applications.