NaNbO 3 -based short-range antiferroelectric ceramics with ultrahigh energy storage performance

Lan Zhang,Zhengu Chen,Gengguang Luo,Fanrong Ai,Nengneng Luo

DOI: https://doi.org/10.1016/j.jeurceramsoc.2023.07.002

IF: 5.7

2023-07-04

Journal of the European Ceramic Society

Abstract:Lead-free NaNbO 3 (NN) antiferroelectric ceramics provide superior energy storage performance and good temperature/frequency stability, which are solid candidates for dielectric capacitors in high power/pulse electronic power systems. However, their conversion of the antiferroelectric P phase to the ferroelectric Q phase at room temperature is always accompanied with large remnant polarization ( P r ), which significantly reduces their effective energy storage density and efficiency. In this study, to optimize the energy storage properties, short-range antiferroelectric (0.95- x )NaNbO 3 - x Bi(Mg 2/3 Nb 1/3 )O 3 -0.05CaZrO 3 ( x BMN) ceramics were designed to stabilize the antiferroelectric phase, in which the local random fields were simultaneously constructed. The results showed that the antiferroelectric orthorhombic P phase was transformed into the R phase, and the local short-range random fields were generated, which effectively inhibited the hysteresis loss and P r . Of great interest is that the 0.12BMN ceramics displayed a large recoverable energy storage density ( W rec ) of 5.9 J/cm 3 and high efficiency ( η ) of 85% at the breakdown strength ( E b ) of 640 kV/cm. The material also showed good frequency stability in the frequency range of 2-300 Hz, excellent temperature stability in the temperature range of 20-110 o C, and a very short discharge time ( t 0.9 ~4.92 μs). These results indicate that x BMN ceramics have great potential for advanced energy storage capacitor applications.

materials science, ceramics