Achieving Ultrahigh Energy Storage Density in Lead-Free Sodium Niobate-Based Ceramics by Modulating the Antiferroelectric Phase
Jiajun Ma,Ji Zhang,Jian Guo,Xiongjie Li,Shun Guo,Yu Huan,Jing Wang,Shan-Tao Zhang,Yaojin Wang
DOI: https://doi.org/10.1021/acs.chemmater.2c01241
IF: 10.508
2022-08-02
Chemistry of Materials
Abstract:Lead-free antiferroelectric ceramics have drawn widespread interest recently on account of their environmentally friendly components and potential applications in high-power systems. However, their relatively low recoverable energy storage density (W rec < 10 J/cm3), limited by the electric breakdown strength (E b < 60 kV/mm), and low efficiency (η < 80%), generated by large hysteresis during the antiferroelectric–ferroelectric phase transition, have seriously restricted their application in portable and compact electronic devices. In this study, the relaxor antiferroelectric (1–x)NaNbO3– x (0.55BiFeO3-0.45SrTiO3) ceramics were elaborately designed and systematically explored. With the help of composition regulation, the ceramics not only exhibited a stable antiferroelectric phase but also underwent a structural transformation from an antiferroelectric P (Pbma) phase to R (Pnma) phase, as confirmed by the temperature-dependent dielectric constants, Raman spectra, X-ray diffraction (XRD) refinement, pinched polarization-electric field (P–E) curves, and four-peak current-electric field (I–E) curves. In addition, the relaxor characteristic was demonstrated by the diffuse dielectric peaks, slim P–E curves, flattened Raman peaks, and I–E curves. Consequently, novel relaxor antiferroelectric ceramics were successfully obtained, which simultaneously revealed the features of relaxor and antiferroelectricity. Specifically, the E b was significantly improved because of the reduced grain size, small sample thickness, exceptionally low dielectric loss, and a moderate dielectric constant. Finally, the sample with x = 0.12 showed an ultrahigh W rec value of 16.2 J/cm3 and satisfactory η of 82.3% at 97 kV/mm, outperforming most state-of-the-art counterparts. Furthermore, the ceramic also exhibited a large current density (C D) of 1268.4 A/cm2 and power density (P D) of 177.6 MW/cm3 at 28 kV/mm, offering prospective applications in high-power capacitors. This work not only achieved outstanding comprehensive energy storage performance in sodium niobate-based ceramics by modulating the antiferroelectric structure but also provided a feasible route to developing high-performance dielectric capacitors from the viewpoint of structure–property relationship.
materials science, multidisciplinary,chemistry, physical