Outstanding Energy Storage Properties under Moderate Electric Field in BiMg2/3Nb1/3O3-modified NaNbO3-based Relaxor Ceramics

Zhenhui Zhang,Xiangluo Miao,Xiangbin Zhang,Shibang Zhang,Changan Wang,Deyang Chen,Min Zeng,Xingsen Gao

DOI: https://doi.org/10.1016/j.ceramint.2024.07.409

IF: 5.532

2024-01-01

Ceramics International

Abstract:NaNbO3 (NN)-based ceramics have received a great deal of attention for the potential application in dielectric energy storage capacitors. However, the energy storage properties (ESP) remain low, particularly under moderate electric field. Herein, a Bi-rich doping unit of BiMg2/3Nb1/3O3 (BMN) was introduced into a 0.85NaNbO(3)-0.15Bi(0.1)Sr(0.85)TiO(3) (NN-SBT) matrix, aiming to improve polarization along ESP. As a result, a large recoverable energy density (W-rec) of similar to 6.1 J/cm(3) and an efficiency (eta) of similar to 81 % were achieved in NN-SBT-0.08BMN ceramics under a moderate electric field of 337 kV/cm. The improved ESP can be attributed to the introduction of BMN, which delays the polarization saturation of NN-SBT ceramics, while maintaining the maximum polarization (similar to 43.6 mu C/cm(2)), and generating polar nanoregions (PNRs). Moreover, the optimal ceramics exhibited good thermal (25-130 degrees C) and frequency (1-300 Hz) stabilities, and fatigue endurance (>10(5) cycles). These results illustrate that the designed NN-SBT-0.08BMN ceramics are promising for application in dielectric energy storage capacitors with high ESP under a moderate electric field.