NaNbO3-based antiferroelectric multilayer ceramic capacitors for energy storage applications

Lovro Fulanović,Mao-Hua Zhang,Yuping Fu,Jurij Koruza,Jürgen Rödel
DOI: https://doi.org/10.1016/j.jeurceramsoc.2021.04.052
IF: 5.7
2021-09-01
Journal of the European Ceramic Society
Abstract:<p>Antiferroelectric materials feature electric-field-induced phase transitions followed by a large polarization change characterized by double polarization hysteresis loops. Therefore, antiferroelectrics are engaging for high-energy density and high-power density applications, especially in the form of multilayer ceramic capacitors (MLCCs). However, the development of lead-free antiferroelectrics with stable double hysteresis loops is still challenging, especially for compositions based on NaNbO<sub>3</sub>. To this end, we have prepared MLCCs with the newly developed antiferroelectric composition 0.90NaNbO<sub>3</sub>-0.06SrSnO<sub>3</sub>-0.04(Na<sub>0.5</sub>Bi<sub>0.5</sub>)TiO<sub>3</sub>. The double hysteresis loops were determined at 24 kV/mm in the temperature range of 25 to 150 °C, with resulting recoverable energy storage ranging from 1.16 to 1.42 J/cm<sup>3</sup>, respectively. Moreover, the energy efficiency is rather constant at 0.4 in the same temperature range. Finally, the MLCCs exhibit resistance to electric field cycling and could withstand up to 1000 cycles. These results verify that NaNbO<sub>3</sub>-based antiferroelectrics in the form of MLCCs are promising for use in applications.</p>
materials science, ceramics
What problem does this paper attempt to address?