Abstract:Copper (Cu) particle sintering is widely regarded as one of the most ideal interconnect technologies for wide band gap semiconductors owing to its potential for low-temperature curing while withstanding a higher working temperature. Nevertheless, the strict requirements for sintering conditions and high costs limit the widespread application of Cu sintering technology. In this paper, a simple vehicle was introduced into Cu paste formulation to achieve an effective sinter bonding even using commercially available sub-micron or even micrometer Cu particles (C-Cu particles) with the in-situ generation of composite Cu particles. This innovative vehicle comprises Cu salt, a combination of capping agents and reducing agents. The addition of the hybrid capping agent binds Cu atoms to the surface of the C-Cu particles and allows the generated Cu particles (G-Cu particles) produced from the vehicle to grow on their surface, resulting in the in-situ generation of composite Cu particles. Based on the in-situ generated composite Cu particles, sintering experiments were conducted at designated temperatures (200 °C, 225 °C, 250 °C) for various durations (3 min, 5 min, 10 min) in a N 2 atmosphere under different pressures (10 MPa, 15 MPa, 20 MPa). A reliable Cu sintered joint with a high shear strength of 41.3 MPa can be achieved at a low temperature (200 °C) using 500 nm C-Cu particles. Moreover, the joints sintered with large size (>3 μm) particles at 250 °C could also reach 43.3 MPa. The in-situ generated composite Cu particles accomplish the transformation of low-energy interfaces of C-Cu/C-Cu to high-energy interfaces of G-Cu/G-Cu, which in turn facilitates low-temperature sintered connection of C-Cu particles and reliable sintered joints formed of large size C-Cu particles. These findings improve the feasibility of Cu sinter bonding in practical applications.

Patterned Cu Nanoparticle Film for All-Cu Interconnection Without Chemical Mechanical Polishing Pretreatment

Interfacial Characterization of Low-Temperature Cu-to-Cu Direct Bonding with Chemical Mechanical Planarized Nanotwinned Cu Films

Cu-Cu bonding by Ag nanostructure at low temperature of 180 °C

Cu-Cu Bonding By Ag Nanostructure At Low Temperature Of 180 Degrees C

Low Temperature Fine-Pitch Wafer-Level Cu-Cu Bonding Using Nanoparticles Fabricated by PVD

Demonstration of Patternable All-Cu Compliant Interconnections with Enhanced Manufacturability in Chip-to-Substrate Applications

Modified Pulse Laser Deposition of Ag Nanostructure As Intermediate for Low Temperature Cu-Cu Bonding

Cu–Cu Bonded Microbump Interconnects with a 10- $\mu$ M Pitch for 3-D-stacked Chiplets

Interfacial Bonding Mechanisms of Sintered Cu Nanoparticles on Different Metallization Surfaces

Preparation of Ag-Cu nanoparticle film using a dual-beam pulsed laser deposition for power electronic packaging

Novel Cu-nanowire-based technology enabling fine pitch interconnects for 2.5D/3D Integration

Rapid and low temperature sintering bonding using Cu nanoparticle film for power electronic packaging

Construction of Microstructures on the Cu Substrate Using Ultrafast Laser Processing to Enhance the Bonding Strength of Sintered Ag Nanoparticles

Micro-cones Cu fabricated by pulse electrodeposition for solderless Cu-Cu direct bonding

Low-Temperature and CMP-Free Direct Bonding of Porous Cu Bumps

Low-temperature Cu Cu Direct Bonding with Ultra-Large Grains Using Highly (110)-Oriented Nanotwinned Copper

Nanocrystalline copper for direct copper-to-copper bonding with improved cross-interface formation at low thermal budget

Enhanced Cu-Cu bonding for ultrahigh-density interconnection: Co passivation bonding with non-oxidation interfaces

Metallurgical aspects and joint properties of Cu-Ni-In-Cu fine-pitch interconnects for 3D integration

High performance Cu sintering joint for power devices enabled by in-situ generation of Cu particles with multi-level hierarchical structures