Abstract:Titanium and its alloys are promising materials for engine production, special pump manufacturing, and bone implants. However, the abrasion resistance and fracture toughness of Ti alloys are insufficient to withstand extreme high loading conditions and harsh environments. Surface modification is an effective way to improve the performance of Ti alloys. In this study, Ag and Cu were added to Ti6Al4V alloy through friction stir processing to modify its surface. The different ratios of the Ag/Cu powder mixture were designed to optimize the surface modification of Ti6Al4V, and the relationship between intermetallic compounds and martensitic transformation was analyzed. The martensitic transformation was induced by AgCuTi phases. The submicron-size martensite was distributed outside the AgCuTi particle, while the nano-laminar martensitic band was generated inside the AgCuTi particle. Under the co-modification of Ti alloy using Ag and Cu, the surface of Ti6Al4V alloy exhibited higher hardness (4.3 GPa) values and lower modulus (100.6 GPa), which gave the credit to the formation of AgCuTi and martensitic transformation. The alloy specimen was subjected to short heat treatment at 600 & DEG;C for 30 min to further modify the gradient structure. After the short heat treatment of the Ag/Cu co-modified specimen, a lower modulus (88.8 GPa) and a high level of hardness (4.1 GPa) were achieved. In addition, superelastic strain recovery was also enhanced, showing the further induced martensitic transformation. This work provides new insight into the surface modification of titanium alloys using the FSP method to achieve the ideal hardness and elastic modulus balance.& COPY; 2023 The Author(s). Published by Elsevier B.V. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).

Intermetallic Compound and Martensitic Transformation in Ag/Cu Co-Modified Ti6Al4V Alloy

Microstructural evolution, mechanical properties and fracture toughness of near β titanium alloy during different solution plus aging heat treatments

Additive manufacturing of titanium alloys with enhanced strength and uniform ductility via multi-element alloying

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Enhanced Mechanical Property of Ti-45551 Alloy Due to TRIP Effect

Unusual Stress-Induced Martensite Transformation in Ti-6Al-4V Alloy Enabled by Solution Treatment in the Lower Α+β Regime

Microstructure and Mechanical Properties of Ti–V–Al–Cu Shape Memory Alloy by Tailoring Cu Content

The Effect of Hf on the Microstructure, Transformation Behaviors and the Mechanical Properties of Ti-Ni-Cu Shape Memory Alloys

In-situ Tailoring Microstructure by Directly Synthesized TiC–TiB2 Nanoparticles to Achieve Well-Balanced Strength and Ductility in Al–Cu Alloy

Drastic enhancement in hot-workability and microstructural refinement of TiAl alloys via martensitic transformation: A comparative study

A Crack-Free Ti-modified Al-Cu Alloy Processed by In-Situ Alloying Laser Powder Bed Fusion: Tribological Behaviors and Mechanical Properties

Achieving low elastic modulus, excellent work hardening and high corrosion resistance in Ti-6Al-4V-5.6Cu alloy

Compositional and Microstructural Optimization and Mechanical-Property Enhancement of Cast Ti Alloys Based on Ti-6Al-4V Alloy

Mechanical Properties of the (Ti0.615zr0.385)100-3.9X(cu2.3fe1.6)x Alloys Containing Amorphous Martensite

Columnar-to-equiaxed transition mechanism and remarkable strengthening effect in additive manufactured pure titanium induced by copper addition

Microstructure Evolution and Mechanical Properties of TiC/Ti6Al4V Medical Composite Processed by Severe Plastic Deformation

Control of Microstructural Characteristics and Martensitic Transformation Behavior of Ti–Ni–Cu Alloys by Pt Doping

In-situ Deformation Mechanisms of a Novel Ti-5Mo-4Cr-1V-1Zr Metastable Β Titanium Alloy

Martensite colony engineering: A novel solution to realize the high ductility in full martensitic 3D-printed Ti alloys

Toughening of Titanium Alloys by Twinning and Martensite Transformation

Influence of Ti addition on microstructure and mechanical behavior of a FCC-based Fe30Ni30Co30Mn10 alloy