Abstract:Aiming at enhancing the electrochemical characteristic of RE-Mg-based composite, the partial substituting La with Ce experiment in the composites was conducted, and the surface modification treatment of the alloys was performed by mechanical coating Ni. By means of mechanical trituration, The La 10-x Ce x Mg 80 Ni 5 (x = 0–2) + y wt% Ni (y = 50–200) compound materials which have the structures of nanocrystalline and amorphous were synthesized. In order to make sense of the principle action of Ce and Ni elements in structural and electrochemical properties of the material, some deep research were carried out. According to the final results, the as-milled composites have the electrochemical hydrogen absorption and hydrogen desorption abilities at room temperature. Having no use for activation, the as-milled composites can reach the maximum discharge capacities when the first cycling was carried out. With the Ni value x changed from 50 to 200, the discharge capacity was varied from 70.5 mAh/g to 902.1 mAh/g; moreover, the capacity retention rate at 20th cycle (S 20 ) and high rate dischargeability (HRD) of the (x = 0) composite were heightened from 67.2 % to 82.3 %, from 50.6 % to 55.7 % respectively. The composites' (y = 100) discharge capacity has a maximum value 118.5 mAh/g when the Ce value x is 1. The capacity retention rate (S 20 ) is enhanced from 53.3 % to 68.5 % by lifting Ce content from x = 0 to x = 2. what's more, the high-rate discharge ability (HRD), the electrochemical impedance spectrum (EIS), potentiodynamic polarization curves, and potential-step measurements all intimate that substituting La with Ce clearly promotes the composites' electrochemical kinetic properties, but maximum values emerge only when the x value is 1.

Preparation of nickel and graphene modified La9CeMg80Ni5 composites and their microstructure and electrochemical properties

Effects of Surface Modification on the Electrode Behavior of Ball-Milled La2Mg17 + 200 Wt% Ni Composite in Alkaline Solution

Electrochemical Properties of Cemg12+X%Ni Composites (X=0 Similar to 200) Prepared by Ball-Milling

Microstructure and Electrochemical Properties of Mechanically Ground Ce2Mg17 + X Wt.% Ni (x = 0, 50, 100, 200) Composites

Electrochemical Properties of CeMg12＋x% Ni Composites （x=0～200） Prepared by Ball-Milling

Microstructures and electrochemical hydrogen storage properties of novel Mg–Al–Ni amorphous composites

Microstructure and electrochemical properties of amorphous composites of ball-milled Mg2Ni0.95Sn0.05 + x wt% Ni

Effect of ball-milling time on the electrochemical performance of ball-milled LaMg11Ni+200wt% Ni composite

Effects of Surface Coating on the Electrochemical Properties of Amorphous CeMg12 Composite

Electrochemical Properties of Cemg11ni+X% Ni Composites (X=0, 50, 100 and 200) Prepared by Ball-Milling

Effects of ball-milling time and Bi2O3 addition on electrochemical performance of ball-milled La2Mg17+200wt.% Ni composites

Microstructure and electrochemical properties of amorphous Mg-Fe-Ni hydrogen storage electrode material

Effect of Ni content on the electrochemical performance of the ball-milled La2Mg17-xNix + 200 wt.% Ni (x = 0, 1, 3, 5) composites

Mechanical Ball Milling Preparation and Electrochemical Hydrogen Storage Properties of Amorphous Mg-Fe Composites

Effects of Surface Modification on the Electrode Behavior of Amorphous CeMg12 Alloys

Influence of Ball-milling with Ni Powder on the Phase Structure and Electrochemical Hydrogen Storage Properties of Mg17Al12 Alloy

Effect of Ce replacing La on the electrochemical performance of amorphous grain boundaries Mg-Ni-based materials

Electrochemical Performance of the Ball-Milled La2Mg14−xTixNi3 Alloys with Ni Powders (x=1 and 2)

Electrochemical properties of amorphous Mg–Fe alloys mixed with Ni prepared by ball-milling

Microstructure and Hydrogen Storage Characteristics of Nanocrystalline Mg+xwt% LaMg2Ni (x=0–30) Composites

The effect of grain refining on the discharge capacity of Mg2Ni/MmNi5-x(CoAlMn)x composite prepared by mechanical alloying