Abstract:Amorphous 2Mg–Fe+xwt.% Ni alloys were synthesized by mechanical alloying of Mg and Fe elemental powders. Two kinds of ball-milling atmospheres, namely, (1) under argon and (2) first under argon and then in tetrahydrofuran (THF), were examined in this study. The effects of the Ni addition and ball-milling time and atmosphere on the microstructure and electrochemical properties of the prepared alloys have been investigated systematically. The results show that the ball-milled (2Mg–Fe) nickel-free mixture still maintains Mg and Fe elemental phases, and its discharge capacity is only 19.2mAhg−1. The Ni powder addition is advantageous for the formation of Mg–Fe amorphous structure and for the improvement of the electrochemical properties of the alloys. For the alloys milled under argon, with the Ni content x increasing, the discharge capacity of the alloys increases first and then decreases, and reaches a maximum value of 455.3mAhg−1 as x=100. With the milling-time extending, the discharge capacity of the alloy increases first and then decreases too. For the alloys milled under argon and then in THF, the alloys exhibit higher degree of amorphorization, bigger specific surface area and more active surfaces, and thus have better electrochemical properties than those milled under argon. With the Ni increasing, the discharge capacity increases from 249.7mAhg−1 (x=50) to 565.2mAhg−1 (x=150) and then decreases to 497.9mAhg−1 (x=200), and the exchange current density I0 increases from 104.8mAg−1 (x=50) to 251.1mAg−1 (x=200), which is consistent with the variation of the HRD of the alloy electrodes in the investigation range.

The effect of grain refining on the discharge capacity of Mg2Ni/MmNi5-x(CoAlMn)x composite prepared by mechanical alloying

Microstructure and electrochemical properties of amorphous composites of ball-milled Mg2Ni0.95Sn0.05 + x wt% Ni

Enhancement of Electrochemical Characteristics of Mg2ni/Mmni(5-X)(Coalmn)(X) by Forming Nano-Phase

Microstructures and electrochemical hydrogen storage properties of novel Mg–Al–Ni amorphous composites

Grain Refining Effect of Magnetic Field on Mg2ni0.8mn0.2 Hydrogen Storage Alloys During Rapid Quenching

Electrochemical Properties of Cemg12+X%Ni Composites (X=0 Similar to 200) Prepared by Ball-Milling

Influence of Ball-milling with Ni Powder on the Phase Structure and Electrochemical Hydrogen Storage Properties of Mg17Al12 Alloy

Microstructure and electrochemical properties of amorphous Mg-Fe-Ni hydrogen storage electrode material

Mechanical Ball Milling Preparation and Electrochemical Hydrogen Storage Properties of Amorphous Mg-Fe Composites

Microstructure and Electrochemical Properties of Mechanically Ground Ce2Mg17 + X Wt.% Ni (x = 0, 50, 100, 200) Composites

An electrochemical investigation of mechanical alloying of MgNi-based hydrogen storage alloys

The effects of mechanical grinding on the hydrogen storage properties of MlNi4.7Al0.3 alloy

Electrochemical properties of amorphous Mg–Fe alloys mixed with Ni prepared by ball-milling

Effect of ball-milling time on the electrochemical performance of ball-milled LaMg11Ni+200wt% Ni composite

Effects of Surface Modification on the Electrode Behavior of Ball-Milled La2Mg17 + 200 Wt% Ni Composite in Alkaline Solution

Research on the Structures and Discharge Capacities of Mg–Ni Alloy with Different Ni Contents Synthesized by High-Energy Ball Milling

Electrochemical Properties of Cemg11ni+X% Ni Composites (X=0, 50, 100 and 200) Prepared by Ball-Milling

Effects of Ni Content on Structure and Discharge Capacities of Mg-Ni Alloy Synthesized by High-Energy Ball Milling

Microstructure and Hydrogen Absorption Properties of Nano-Phase Composite Prepared by Mechanical Alloying of MmNi5−x(CoAlMn)x and Mg

Electrochemical Properties of CeMg12＋x% Ni Composites （x=0～200） Prepared by Ball-Milling

The Effect of Mg Content on Microstructure and Hydrogen Absorption Properties of Mechanical Alloyed MmNi3.5(CoAlMn)1.5–Mg