Strengthening contributions of mechanical twinning and dislocations to the flow stress of 1.1C-12.5Mn steel at a strain rate of unity per second: Quantitative analysis

Mahmoud Khedr,Wei Li,Na Min,Walaa Abd-Elaziem,Xuejun Jin

DOI: https://doi.org/10.21203/rs.3.rs-1499180/v1

2022-01-01

Abstract:Abstract The flow stress of high C-Mn austenitic steel is attributed to lattice friction, dynamic strain aging (DSA), mechanical twinning and forest hardening. However, it has not been clarified yet which mechanism quantitatively contributes most to the work hardening of 12.5Mn-1.1C steel. In this study, austenitic Hadfield steel (1.1 wt.% C and 12.5 wt.% Mn) was tensile tested at a strain rate of 10⁰ s− 1. The lattice friction was estimated by the Hall-Petch relationship. DSA effect was neglected because of the high strain rate of deformation. Twin plates characteristics and dislocation densities were estimated quantitatively at different strain levels (11, 18, 25, 38, and 55%). The deformed twin plates were studied by optical and transmission electron microscopies. Dislocation densities were estimated by analyzing the X-ray diffraction patterns using Rietveld analyses. A linear approach was utilized to model the flow stress during the plastic deformation, and it is found that the linear model is consistent with the experimental results. During the early stages of the plastic deformation, the mechanical twinning was the dominant deformation mechanism, and it was more effective to the flow stress than the forest hardening due to the enhancement of the twin nucleation process. However, with increasing the strain level, the thicknesses of the twinned plates were increased rather than the initiation of new twin plates, resulting in a reduced contribution by the mechanical twinning to the flow stress. On the other hand, increasing the dislocation densities with an increase in the strain level was detected, which resulted in an enhanced contribution by forest hardening to the flow stress more than the mechanical twinning.