Microstructure evolution and shearing behaviour of δꞌ/θꞌ/δꞌ precipitates in an aged Al-Cu-Li-Mg aluminium alloy

Hongxing Li,Chien-Nan Hsiao,Jer-Ren Yang,Cheng-Si Tsao,Takahito Ohmura,Chung Tsai-Fu,Lin Shan-Qiao
DOI: https://doi.org/10.1016/j.jallcom.2023.170095
IF: 6.2
2023-04-20
Journal of Alloys and Compounds
Abstract:We report here on the microstructure evolution and the strengthening behaviour of the δꞌ/θꞌ/δꞌ precipitates in the aged Al-Cu-Li-Mg aluminium alloy by atomic high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and in-situ TEM compression straining. On the chosen zone axis, atomic HAADF-STEM images reveal the in-situ microstructure evolution of the δꞌ/θꞌ/δꞌ precipitates. A monolayer GP(θꞌ) zone, grown on the (001) Al plane, evolves from the Cu-rich region. After the transformation of the GP(θꞌ) zone to θꞌ phase, the boundaries of the θꞌ phase are coated with the δꞌ phases, forming a matured δꞌ/θꞌ/δꞌ precipitate. Additionally, the growth of δꞌ phases on the two sides of θꞌ is not affected by the inclined boundaries of θꞌ and the hard impingement of the thin T 1 precipitate. During the in-situ TEM compression straining on the peak-aged nanopillar, the deviated slip band structures and the large displacement bursts are presumably associated with the dislocation-precipitate interaction of the T 1 and δꞌ/θꞌ/δꞌ precipitates. Furthermore, evidence from atomic HAADF-STEM images shows that dislocations can cut the δꞌ/θꞌ/δꞌ precipitate, producing the stacking fault layers within the θꞌ phase of the sheared δꞌ/θꞌ/δꞌ precipitate.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?