Environmentally-Assisted Fatigue at Small Scales

Zhiping Xu

DOI: https://doi.org/10.1016/b978-0-12-822944-6.00090-6

2022-01-01

Abstract:Fatigue as a mechanical process of material degradation is the result of microstructural evolution and damage accumulation under fluctuating loading conditions. The progressive deterioration of material strength in fatigue can be regulated by chemistry, temperature and pressure of the environment. The notion of environmentally-assisted fatigue (EAF) is closely related to engineering problems such as stress corrosion cracking (SCC), hydrogen embrittlement (HE), and corrosion fatigue (CF). The integration of environmental effects into the initiation and propagation of fatigue cracks introduces interplay between deformation, failure of materials and transport, reaction of chemical species. The whole process is usually very complex and sensitive to the materials and environment. Exploring the process of EAF at small scale allows to identify the key physical processes by excluding the microstructural and environmental complexities of materials. On the other hand, EAF was also shown to be a detrimental process for the micro- and nanostructures, where the environmental effects become even more significant for the reduced dimension and large surface-to-volume ratios. The presentation will be focused on the general principles that improve the understanding and prediction of material behaviors under environmental attacks. Section “Physics of Environmentally-Assisted Fatigue” outlines the fundamentals of fatigue and the environmental effects, which lays the ground for following discussions. Section “Techniques and Methods” introduces the experimental and simulation techniques that are used to resolve the complexity of EAF at small scales. Section “Environmentally-Assisted Fatigue at Small Scales” summarizes the state-of-the-art knowledge of EAF at small scale, followed by a list of perspectives in Section “Summary and Outlook”.