Abstract:In this study, the waste silicon powder generated in the production of solar-grade polysilicon scrap was used as the raw material, and silicon nitride (Si3N4) was directly efficient prepared by the microwave heating nitridation. The temperature raising characteristics of silicon powder by microwave heating and the influencing factors of the nitridation reaction process were studied. The thermogravimetric analysis was performed, and the temperature raising dielectric properties of silicon powder were studied. The electromagnetic field and temperature distributions of the microwave heating-induced silicon powder nitridation process were simulated using COMSOL software. The nitridation reaction of silicon powder induced by microwave heating has better temperature raising characteristics: the average heating rate can reach 135 °C/min, and the reaction time is significantly shortened (only 10-20 min). Microwave heating decreases the nitridation reaction temperature by more than 100 °C and greatly shortens the reaction time. With the increase of nitrogen pressure and reaction time, the nitridation reaction is better. In addition, the conversion of the nitridation reaction is more than 97%, and the products are mainly β-Si3N4 with the uniform and columnar morphology. Finally, it is proved that the efficient recovery and utilization of industrial waste silicon powder are realized, and there is lower energy consumption by microwave heating technology.

Synthesis of Spherical-Like Β-Si3n4 Powder by Direct Nitridation of Silicon Saw Dust

Synthesis of Spherical Si3N4 Powders by Liquid‐phase Modified Carbothermal Reduction and Nitridation

Synthesis of monodisperse and high-purity α-Si3N4 powder by carbothermal reduction and nitridation

Synthesis of Si 3 N 4 powder with tunable α/β-Si 3 N 4 content from waste silica fume using carbothermal reduction nitridation

Synthesis and Growth Mechanism of Approximate Spherical Β‐si3n4 Particles Via Carbothermal Reduction‐nitridation Method

Preparation of silicon nitride powder from silica and ammonia

Liquid-Phase-Assisted Catalytic Nitridation of Silicon and In Situ Growth of α-Si3N4

Synthesis of β-Si3N4 powder from quartz via carbothermal reduction nitridation

Additive-Assisted Nitridation to Synthesize Si<sub>3</sub>N<sub>4</sub>Nanomaterials at a Low Temperature

Synthesis of Well-Dispersed Columnar Si 3 N 4 Using Carbothermal Reduction–nitridation Method

Additive‐Assisted Nitridation to Synthesize Si3N4 Nanomaterials at a Low Temperature

Synthesis and Growth Mechanism of Single Crystal Β‐si3n4 Particles with a Quasi‐spherical Morphology

Preheating-assisted Combustion Synthesis of Β-Si3n4 Powders at Low N2 Pressure

Efficient Preparation of Si3N4 by Microwave Treatment of Solar-Grade Waste Silicon Powder

Research of Silicon Nitride Powder Prepared by Self-propagating High-temperature Synthesis

Synthesis of Single-Crystalline Α-Si3n4nanobelts by Extended Vapour–liquid–solid Growth

Sulfur-assisted Fabrication of Silicon Nitride Nanorods in Autoclaves at 250 °C

Synthesis of alpha-Si3N4 whiskers or equiaxed particles from amorphous Si3N4 powders

Synthesis of well-dispersed β-Si3N4 with equiaxed structures using carbothermal reduction–nitridation method

Precisely Controlled Carbothermal Synthesis of Spherical Β-Si3n4 Granules

Carbothermal Synthesis Of Micron-Sized Beta-Si3n4 With Tailored Morphology