Abstract:To investigate the feasibility of preparing CaO-SiO2-Al2O3 inorganic fibers with melting-separated red mud, the properties of the melting-separated red mud were analyzed by X-ray fluorescence, X-ray diffraction, and differential thermal-thermogravimetric analyses. The composition of the melting-separated red mud satisfied the requirements for the composition of inorganic fibers. During the melting of the melting-separated red mud, tetrahedral skeleton fracture reactions occurred at 1,234 degrees C, anionic group reverse binding occurred at 1,250 degrees C, and there was no other obvious reaction peak during the whole melting process, which lasted for 51 min. The minimum suitable fiber forming temperature of the melting-separated red mud melt was 1,433 degrees C, which was 83 degrees C greater than its crystallization temperature, 1,350 degrees C. Within this temperature range, the activation energy of particle movement in the melt was 1008.65 kJ.mol(-1), and the melt exhibited good fluidity. Considering the temperature distribution corresponding to the melting properties of the melting-separated red mud, CaO-SiO2-Al2O3 inorganic fibers could be prepared when the melting-separated red mud was subjected to component reconstruction by increasing the silicon content, reducing the aluminum content, and adding a moderate amount of calcium. Quartz sand and light burnt dolomite were used as modifying agents and inorganic fibers were prepared under laboratory conditions. The fibers prepared from the modified melting-separated red mud by adding different amounts of melting-separated red mud had smooth surfaces and were arranged in a crossed manner at the macroscopic level. Their color was grayish-white, and small quantities of slag balls were doped inside the fibers. With an increase in the amount of melting-separated red mud from 50 to 100%, the average fiber diameter increased from 5.5 to 8.0 mu m, and their slag ball content increased from 2.9 to 6.0%. Overall, under laboratory conditions, when the amount of melting-separated red mud added was 50%, dolomite was 22.5% and quartz sand was 27.5%, the performance of the fiber was the best.

Preparation of CaO–SiO2–Al2O3 Inorganic Fibers from Melting-Separated Red Mud

Investigation of Preparation of Slag Wool from Melting-Separated Red Mud

Numerical Simulations of the Impact of CaO/Al2O3 on the Structure and Crystallization Behavior of Red Mud

Fabrication of Y2O3-doped MgO Refractory Raw Materials Based on Magnesium Hydroxide from Salt-Lake Brine

Synthesis and Characterization of Rich Silica Mullite Fibers by Sol–Gel Method Using Aluminum Lactate and Silica Sol

Extraction of Aluminum and Preparation of Polymerized Aluminum Ferric Sulfate from Red Mud

High‐efficiency Preparation of Fe–Al Based Flocculants from Red Mud by Microwave Selective Carbothermic Reduction and Magnetic Separation

Experimental Study on Preparation of Inorganic Fibers from Circulating Fluidized Bed Boilers Ash

Preparation and characterization of SiO2–Al2O3–MgO–CaO–based ceramic foams mainly from Ca–Mg–rich molybdenum tailings

Mullite Fibers Prepared by Sol-Gel Method Using Aluminum Chloride Aluminum Isopropoxide and Tetraethylorthosilicate

Study Progress on Inorganic Fibers from Industry Solid Wastes and the Key Factors Determining Their Characteristics

Preparation of Mullite Fibers by Sol-Gel Process and Study of Their Morphology

Mullite Fibers Prepared from an Inorganic Sol–gel Precursor

Preparation and performance of ceramic filter material by recovered silicon dioxide as major leached component from red mud

Extraction of Iron and Alumina from Red Mud with a Non-Harmful Magnetization Sintering Process

Thermodynamic Simulation on Mineralogical Composition of CaO–SiO2–Al2O3–MgO Quaternary Slag System

Microwave Absorption Performance of in Situ Synthesized Fe3O4-SiO2 Hybrid Fibres with Enhanced Environmental Stability

Modulating red mud for the fabrication of cementitious material by analyzing the thermal evolution of hydrogarnets

Mechanical properties of high ductile alkali-activated fiber reinforced composites incorporating red mud under different curing conditions

Effect of the alumina and silica source mixing procedure on the microstructural evolution of alumina-mullite composite fibers prepared by sol–gel method

Preparation of continuous silicate fiber from pyroxene and K-feldspar mixture