The dynamic recrystallization behavior of the Ti-5.5Mo-7.2Al-4.5Zr-2.6Sn-2.1Cr titanium alloy during hot rolling based on macro-meso multiscale crystal plasticity finite element approach
Duoduo Wang,Hongwei Li,Xujie Song,Yan Ren,Qunbo Fan,Xinjie Zhu,Lihua Chen,Yanchun Wang,Wei Gao,Zhibo Cao,Sitao Wang,Peili Gao
DOI: https://doi.org/10.1016/j.mtcomm.2023.106555
IF: 3.8
2023-06-29
Materials Today Communications
Abstract:The understanding of dynamic recrystallization under complex thermo-mechanical coupling is still a technical challenge. Therefore, in this work, combining the Johnson-Mehl-Avrami-Kolmogorov recrystallization grain model, a macro-meso multiscale crystal plasticity finite element approach was innovatively proposed. The isothermal hot compression test was performed to obtain the true stress-strain curves of Ti-5.5Mo-7.2Al-4.5Zr-2.6Sn-2.1Cr titanium alloy (strain rates: 0.001 s -1 , 0.01 s -1 , 0.1 s -1 , 1 s -1 , and 10 s -1 ; temperatures: 650 °C, 700 °C, 750 °C, 800 °C, and 850 °C). Afterward, corresponding fitted parameters can be used to update the volume fraction and size of recrystallized grains of each sub-step. The macro simulation results showed that the surface layer had prominent strain partitioning and lower equivalent stress after hot rolling (thickness reduction: 60%). For the region of interest, the calculated volume fraction and equivalent circle diameter of recrystallized grains were 2.45% and ~1 μm, respectively, which were in good agreement with the experimental results.
materials science, multidisciplinary