Abstract:Developing ultra-high strength in rare-earth-free Mg alloys using conventional extrusion process is a great challenge. What is even more difficult is to achieve such a goal at a lower processing cost. In this work, we report a novel low-alloyed Mg-2Sn-2Ca alloy (in wt. %) that exhibits tunable ultra-high tensile yield strength (360–440 MPa) depending on extrusion parameters. More importantly, there is little drop in mechanical properties of this alloy even when it is extruded at a speed several times higher than those used in the reported high strength Mg alloys. Examination of as-extruded microstructures of this Ca-containing Mg alloy reveals that the ultra-high strength is mainly associated with the presence of surprisingly submicron matrix grains (down to ∼0.32 μm). The results suggest that the Ca addition promotes accumulations of the pyramidal dislocations, which eventually transform into the low angular grain boundaries (LAGBs). The high number density of LAGBs separate the α-Mg matrix via either discontinuous dynamic recrystallization (DDRX) mechanism in the early stage or the continuous dynamic recrystallization (CDRX) mechanism in the later stage of extrusion, which effectively enhances the nucleation rates of the DRXed grains. More importantly, large amount of Ca segregation along LAGBs, accompanied with dynamically precipitated Mg2Ca nano-phases, are detected in the present non-severely deformed samples. It is the combination of solute segregations and numerous Mg2Ca nano-precipitates that contributes to the formation of the ultra-fine grains via pinning mechanism. The ultrafine grains size, Ca enrichment in most LAGBs, and residual Mg2Ca nano-precipitates would in turn contribute significantly to the enhancement of the yield strength of the as-extruded Mg-2Sn-2Ca (wt.%) alloy. The low content of alloying elements and the fast one-step extrusion process render the present alloys low-cost and thus have great potential in large-scale industry applications.

Preparing a Dilute Mg-Mn-Zn Alloy with Ultra-High Strength by Coupling Extrusion and Forging at Low Temperatures

Realizing ultra-fine grains and ultra-high strength in conventionally extruded Mg-Ca-Al-Zn-Mn alloys: The multiple roles of nano-precipitations

Achieving superior mechanical properties in a low-alloyed magnesium alloy via low-temperature extrusion

Ultrahigh Strength Mg-Al-Ca-Mn Extrusion Alloys with Various Aluminum Contents

Preparation of ultrafine-grained Mg–Mn–Ce alloy with high ductility and energy absorption by coupling extrusion and forging

Ultra-high strength Al-Zn-Mg-Cu alloys with high zinc content prepared via powder hot extrusion

Fine-grained Mg–1Mn–0.5Al–0.5Ca–0.5Zn alloy with high strength and good ductility fabricated by conventional extrusion

On Mechanical Properties and Superplasticity of Mg–15Al–1Zn Alloys Processed by Reciprocating Extrusion

Developing Mg-Gd-Dy-Ag-Zn-Zr Alloy with High Strength via Nano-Precipitation

Low-cost and high-strength Mg-Al-Ca-Zn-Mn wrought alloy with balanced ductility

Ultra strength-ductility synergy in the Mg-Al-Zn alloy via densely dispersed multi-scale {10<mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML" altimg="si1.svg"><mml:mrow><mml:mover accent="true"><mml:mn>12</mml:mn><mml:mo>¯</mml:mo></mml:mover></mml:mrow></mml:math>} tension twins

Exploiting an as-extruded fine-grained Mg-Bi-Mn alloy with strength-ductility synergy via dilute Zn addition

Achieving Low Tension-Compression Yield Asymmetry and Ultrahigh Strength in Mg–1Al–1Ca–0.2Mn (wt%) Alloy Via Sub-Micron Grain Refinement

Approaching 1 GPa ultra‐high tensile strength in a nanostructured Al‐Zn‐Mg‐Cu‐Zr‐Sc alloy prepared by severe plastic deformation

Achieving exceptional ultrahigh-strength in low-alloy Mg-1Al-1Ca-0.4Mn (wt%) alloy by regulating bimodal microstructure

Achieving Ultra-High Strength in Mg–Gd–Ag–Zr Wrought Alloy Via Bimodal-Grained Structure and Enhanced Precipitation

Enhanced Thermal Conductivity and Mechanical Properties of Extruded Mg-4La-2Al-0.3Mn Alloy Via Hot Forging

Development of low-alloyed and rare-earth-free magnesium alloys having ultra-high strength

Tailoring strength and ductility of Mg97Y2Zn1 alloy through the architecture of heterogeneous lamellar structure by large-ratio hot extrusion

Improving Strength and Ductility of Mg–Gd–Y–Zn–Zr Alloy Simultaneously Via Extrusion, Hot Rolling and Ageing

Development of ultrahigh-strength low-alloy Mg-0.7Al-0.3Ca-0.4Mn (wt.%) alloy with excellent ductility via controlling extrusion temperature