Preparation of high molecular weight polypropylene glycol in microchannel reactor

ZHANG Xueting,HU Jijiang,ZHAO Jing,LI Bogeng

DOI: https://doi.org/10.11949/0438-1157.20221630

2023-01-01

Abstract:High molecular weight polyether polyols are widely used. However, there is not only a large risk of reaction heat, but also a long reaction time in its traditional production process by using the semi-continuous reactor. The microchannel reactor（MCR） has the characteristics of high heat transfer efficiency and process safety,but the viscous material and high reaction heat release make it difficult to produce the high molecular weight polyether polyols. In this work, using double metal complex（DMC） as catalyst and n-hexane as solvent, the ringopening polymerization of propylene oxide（PO） was carried out in MCR. Polypropylene glycol（PPG） with molecular weight ranging from 2000 to 8000 was prepared. Effects of reaction conditions, such as flow rate, channel length,reaction temperature and feed policy, were investigated. It has been found that when the residence time is long enough, the molecular weight of the produced PPG is basically equal to the theoretical molecular weight. When the flow rate of initiator is fixed, an increase in flow rate of monomer will result in the molecular weight distribution（MWD） first widened and then narrowed. If the tube length is longer, the molecular weight is larger and the MWD is wider. If the temperature increases, the induction period of the polymerization can be shortened. Using the segmented feed, it is easier to prepare high molecular weight PPG with higher conversion than using the single feed, but the MWD is wider. These rules can be explained from the mechanism of PO ring-opening polymerization catalyzed by DMC and micro-mixing strength of materials in MCR. The lower the micro-mixing strength, and the smaller the rate ratio of chain transfer to chain propagation in polymerization, the wider the molecular weight distribution is.