Abstract:The structural differences at various positions in the GH3625 alloy before and after magnesium treatment were statistically analyzed. In situ observation experiments were conducted at different cooling rates to examine the changes in solidification structure following magnesium treatment. A new theoretical explanation for the differential effects of magnesium treatment was proposed based on classical homogeneous nucleation theory. In practical applications, intermetallic compounds like Laves phase and metal carbides adversely affect the performance of nickel‐based superalloys. Using a high‐temperature confocal laser scanning microscope, the solidification process of as‐cast GH3625 alloy containing Mg at different cooling rates (−20, −35, and −50 °C min−1) is studied. Fitting curves of the volume fraction of the solid phase with solidification temperature before and after Mg treatment are obtained. Trends of solid phase transformation rates with solidification temperature are determined. Differential scanning calorimetry is employed to analyze and statistically evaluate the melting temperature range and enthalpy of each phase during the melting process. Experimental results demonstrate that Mg treatment significantly accelerates the alloy solidification at the cooling rates of −20 and −35 °C min−1, while reducing the area of residual liquid phase at the same solidification temperature, disrupting the Laves/NbC eutectic relationship, and regularizing NbC morphology, transitioning its distribution from aggregation to dispersion. After Mg treatment, the precipitation of the Laves phase is significantly reduced. As a result, the influence mechanism of Mg treatment on the phase transformation and microstructure of GH3625 is clarified based on homogeneous nucleation theory.

As-cast Microstructure and Homogenization Kinetics of a Typical Hard-to-deform Ni-base Superalloy

Microstructure Evolution and Homogenization Kinetics of 15Cr–30Ni–Fe Heat‐Resistant Alloy

Incipient melting phase and its dissolution kinetics for a new superalloy

Investigation of Solidification Behavior in a New High Alloy Ni-Based Superalloy

Phase constitution, microstructure and mechanical properties of a Ni-based superalloy specially designed for additive manufacturing

In Situ Observation of Microstructure and Precipitate Phase Transformation during the Solidification of Mg‐Containing GH3625 Alloy at Different Cooling Rates

Microstructure Evolution and Mechanical Properties of NiAlCrFeMo High Entropy Superalloy after Different Annealing Treatment

The influence of homogenization on the microstructure and high-temperature mechanical properties of ERNiCrMo-3 alloy

Microstructural Evolution of Wrought-Nickel-Based Superalloy GH4169

Experimental Investigation on Recrystallization Mechanism of a Ni-base Single Crystal Superalloy

Microstructure and Microsegregation in A Ni-Based Single Crystal Superalloy Directionally Solidified under High Thermal Gradient

Temperature-Dependent Mechanical Behaviors and Deformation Mechanisms in a Si-Added Medium-Entropy Superalloy with L12 Precipitation

Microstructures and homogenization behavior of a nickel-based superalloy used for 850¬Ý‚ÑÉ turbine disc prepared by electron beam smelting layered solidification

Microstructure evolution behavior of Ni3Al (γ′) phase in eutectic γ-γ′ of Ni3Al-based alloy

Effect of alloying on the microstructure, phase stability, hardness and partitioning behavior of a new dual-superlattice nickel-based superalloy

Hot deformation behavior and flow stress modeling of coarse-grain nickel-base GH4151 superalloy ingot materials in cogging

Multiphase-field and experimental study of solidification behavior in a nickel-based single crystal superalloy

Hot Deformation Characteristics and Dynamic Recrystallization Mechanisms of a Novel Nickel‐Based Superalloy

Processing, Microstructures and Mechanical Properties of a Ni-Based Single Crystal Superalloy

Microstructural Evolution of a High W Content Ni-Based Superalloy at γ′ Sub-Solvus Temperatures

Experimental Study on the Micro-Mechanical Parameters of Ni-based Single-Crystal Superalloys Using Nanoindentation and Element Distribution Analysis