Hot Deformation Characteristics and Dynamic Recrystallization Mechanisms of a Novel Nickel‐Based Superalloy

Shaomin Lv,Chonglin Jia,Xinbo He,Zhipeng Wan,Yang Li,Xuanhui Qu
DOI: https://doi.org/10.1002/adem.202000622
IF: 3.6
2020-08-02
Advanced Engineering Materials
Abstract:<p>The hot deformation characteristics of a novel nickel‐based superalloy was investigated via the isothermal compression test in temperature range of 1000‐1150 ℃ and strain rate of 0.001‐10 s<sup>−1</sup> under the true strain of 0.8. The hot deformation characteristics of GH4065 alloy were studied here for the first time in order to determine the optimal hot deformation parameters and regulate the microstructure under different deformation conditions. Based on the flow stress data, it is observed the typical features of flow curves exhibited the occurrence of dynamic recrystallization (DRX) during the hot deformation process. The constitutive equation in the Arrhenius‐type model was established, and activation energy (<i>Q </i>) was determined as 844.787 kJ/mol. The microstructure evolution and DRX mechanism were investigated by electron backscatter diffraction (EBSD) and transmission electron microscope (TEM) technique. The results revealed that the fraction of low angle grain boundaries (LAGBs) decreased gradually with the increase of deformation temperature, while the fraction of Σ3 boundaries increases firstly and then decreases. For γ<i>+ </i>γ<i>' </i> dual‐phase region, the particle‐induced DRX (PIDRX), characterized by the generation of sub‐grains accelerated by γ<i>' </i> precipitates pinning dislocations, and DDRX were the dominant nucleation mechanism of DRX. For γ quasi‐phase region and γ single‐phase region, the occurrence of bulged grain boundaries with twins further illustrates that DDRX plays a more significant role.</p><p>This article is protected by copyright. All rights reserved.</p>
materials science, multidisciplinary
What problem does this paper attempt to address?