Regulating the Grain Orientation and Surface Structure of Primary Particles through Tungsten Modification to Comprehensively Enhance the Performance of Nickel-Rich Cathode Materials
Wenjin Li,Jian Zhang,Yunan Zhou,Wei Huang,Xianghuan Liu,Zhao Li,Min Gao,Zenghua Chang,Ning Li,Jiantao Wang,Shigang Lu,Xiaolong Li,Wen Wen,Daming Zhu,Yan Lu,Weidong Zhuang
DOI: https://doi.org/10.1021/acsami.0c12893
2020-09-25
Abstract:Nickel-rich layered oxides, as the most promising commercial cathode material for high-energy density lithium-ion batteries, experience significant surface structural instabilities that lead to severe capacity deterioration and poor thermal stability. To address these issues, radially aligned grains and surface Li<sub><i>x</i></sub>Ni<sub><i>y</i></sub>W<sub><i>z</i></sub>O-like heterostructures are designed and obtained with a simple tungsten modification strategy in the LiNi<sub>0.91</sub>Co<sub>0.045</sub>Mn<sub>0.045</sub>O<sub>2</sub> cathode. The formation of radially aligned grains, manipulated by the WO<sub>3</sub> modifier during synthesis, provides a fast Li<sup>+</sup> diffusion channel during the charge/discharge process. Moreover, the tungsten tends to enter into the lattice of the primary particle surface, and the armor-type tungsten-rich heterostructure protects the bulk material from microcracks, structural transformations, and surface side reactions. First-principles calculations indicate that oxygen is more stable in the surface tungsten-rich heterostructure than elsewhere, thus triggering an improved surface structural stability. Consequently, the 2 wt % WO<sub>3</sub>-modified LiNi<sub>0.91</sub>Co<sub>0.045</sub>Mn<sub>0.045</sub>O<sub>2</sub> () material shows outstanding prolonged cycling performance (capacity retention of 80.85% after 500 cycles) and excellent rate performance (5 C, 188.4 mA h g<sup>–1</sup>). In addition, its layered-to-rock salt phase transition temperature is increased by 80 °C compared with that of the pristine cathode. This work provides a novel surface modification approach and an in-depth understanding of the overall performance enhancement of nickel-rich layered cathodes.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c12893?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c12893</a>.SEM images of the raw materials; SEM images of the intermediate materials; SEM images for the lithiated cathode materials; cross-sectional images; TEM images with EDS mapping and line scans; XRD patterns for the lithiated cathode materials; Rietveld fitting results for the XRD patterns; DFT calculation models of a W atom in different substitution sites; XPS spectra and fitting results; electrochemical performance between 2.5 and 4.3 V; electrochemical performance between 2.7 and 4.5 V; full pouch-type cell cyclability; GITT curves; cyclic voltammogram curves; in situ XRD patterns during the charging process; X-ray diffraction patterns after 200 cycles; equivalent circuit of EIS fitting; schematic illustration of the fading mechanism; in situ XRD patterns during the heating experiment; DSC profiles; TG/DSC profiles; DFT calculation models in different sites; ICP-AES results; crystallographic results; XPS fitting results; cycling performance results; rate performance results; GITT results; comparison of electrochemical performance results; EIS results; and charges gain/loss results (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c12893/suppl_file/am0c12893_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology