Regulating the Grain Orientation and Surface Structure of Primary Particles through Tungsten Modification to Comprehensively Enhance the Performance of Nickel-Rich Cathode Materials

Wenjin Li,Jian Zhang,Yunan Zhou,Wei Huang,Xianghuan Liu,Zhao Li,Min Gao,Zenghua Chang,Ning Li,Jiantao Wang,Shigang Lu,Xiaolong Li,Wen Wen,Daming Zhu,Yan Lu,Weidong Zhuang

DOI: https://doi.org/10.1021/acsami.0c12893

2020-09-25

Abstract:Nickel-rich layered oxides, as the most promising commercial cathode material for high-energy density lithium-ion batteries, experience significant surface structural instabilities that lead to severe capacity deterioration and poor thermal stability. To address these issues, radially aligned grains and surface Li_<i>x</i>Ni_<i>y</i>W_<i>z</i>O-like heterostructures are designed and obtained with a simple tungsten modification strategy in the LiNi_0.91Co_0.045Mn_0.045O₂ cathode. The formation of radially aligned grains, manipulated by the WO₃ modifier during synthesis, provides a fast Li⁺ diffusion channel during the charge/discharge process. Moreover, the tungsten tends to enter into the lattice of the primary particle surface, and the armor-type tungsten-rich heterostructure protects the bulk material from microcracks, structural transformations, and surface side reactions. First-principles calculations indicate that oxygen is more stable in the surface tungsten-rich heterostructure than elsewhere, thus triggering an improved surface structural stability. Consequently, the 2 wt % WO₃-modified LiNi_0.91Co_0.045Mn_0.045O₂ () material shows outstanding prolonged cycling performance (capacity retention of 80.85% after 500 cycles) and excellent rate performance (5 C, 188.4 mA h g^–1). In addition, its layered-to-rock salt phase transition temperature is increased by 80 °C compared with that of the pristine cathode. This work provides a novel surface modification approach and an in-depth understanding of the overall performance enhancement of nickel-rich layered cathodes.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c12893?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c12893</a>.SEM images of the raw materials; SEM images of the intermediate materials; SEM images for the lithiated cathode materials; cross-sectional images; TEM images with EDS mapping and line scans; XRD patterns for the lithiated cathode materials; Rietveld fitting results for the XRD patterns; DFT calculation models of a W atom in different substitution sites; XPS spectra and fitting results; electrochemical performance between 2.5 and 4.3 V; electrochemical performance between 2.7 and 4.5 V; full pouch-type cell cyclability; GITT curves; cyclic voltammogram curves; in situ XRD patterns during the charging process; X-ray diffraction patterns after 200 cycles; equivalent circuit of EIS fitting; schematic illustration of the fading mechanism; in situ XRD patterns during the heating experiment; DSC profiles; TG/DSC profiles; DFT calculation models in different sites; ICP-AES results; crystallographic results; XPS fitting results; cycling performance results; rate performance results; GITT results; comparison of electrochemical performance results; EIS results; and charges gain/loss results (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c12893/suppl_file/am0c12893_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology

What problem does this paper attempt to address?

The paper attempts to address the significant surface structural instability issues faced by nickel-rich layered oxide cathode materials when the nickel content exceeds 90%, which leads to severe capacity degradation and poor thermal stability. Specifically, the paper focuses on enhancing the performance of nickel-rich layered oxide cathode materials by regulating the grain orientation and surface structure of primary particles through a tungsten modification strategy.

The paper mentions that with the increase in nickel content, nickel-rich layered oxides undergo a gradual multiphase transformation (from layered structure to spinel structure, and then to rock-salt structure) from the surface to the bulk during long-term charge-discharge processes or under overheating conditions, accompanied by oxygen release and loss of active material/lithium. Additionally, the highly active surface Ni4+ ions formed during charging easily react with the electrolyte, further exacerbating the performance degradation of the material. Therefore, the paper proposes a simple and effective tungsten modification method, which involves adding nano-sized tungsten trioxide (WO3) during synthesis to promote the formation of radially aligned grains and form a Li xNiyWzO-like heterostructure on the surface of the cathode material, thereby improving the material's cycling performance, rate performance, and thermal stability. Experimental results show that the LiNi0.91Co0.045Mn0.045O2 (NCM@2W) material modified with 2wt% WO3 retains 80.85% of its capacity after 500 cycles and achieves a specific capacity of 188.4 mAh g-1 at 5C. Furthermore, its layered to rock-salt phase transition temperature is increased by 80°C compared to the unmodified cathode. These findings not only provide a new surface modification method but also deeply reveal the mechanism of interface structure modification and performance enhancement by tungsten doping.