Effect of Hot Torsion on Microstructure and Properties of Precipitation Hardening Martensitic Stainless Steel

Liu Yixiang,Wang Hao,Zhao Yinglong,Hou Xiang,Wang Xiaoli,Xia Huijie,Song Bo,Chai Linjiang,Guo Ning,Guo Shengfeng

DOI: https://doi.org/10.1007/s11665-023-08029-7

IF: 2.3

2024-01-01

Journal of Materials Engineering and Performance

Abstract:In this study, a 14.4Cr-13.9Co-4.9Mo-0.5 V precipitation hardening steel was twisted by free-end torsion at various temperatures. The microstructure of the twisted samples at different strained layers was characterized by the combined use of x-ray diffraction, electron channeling contrast imaging, and electron backscatter diffraction techniques. Results show that at room temperature, the samples exhibit higher deformation resistance but lower ductility, and the twisted samples have a gradient distribution of dislocation density from the core to the surface. There is no phase transformation during torsion. When twisted at 300-500 °C, the samples exhibit lower yield strength but higher ductility. With increasing temperature, the ductility and the deformation resistance gently decrease. The reverse transformation of martensite to austenite occurs during hot-torsion at above 300 °C. Torsion can promote the transformation of martensite to austenite under heating. Under heating conditions, torsional shear strain helps to promote the formation of the reversed austenite. Whether at room temperature or high temperature, the microhardness showed a gradient distribution from the core to the surface. The gradient distribution of hardness is related not only to shear strain but also to the reversely transformed austenite content.