Abstract:AISI 317 L stainless steel replaces 316 L grade in some applications due to its superior mechanical strength and corrosion resistance. Aiming at expanding its applicability to structural applications, ongoing studies are dedicated to overcoming the trade-off between strength and ductility. The stacking fault energy decreases with deformation temperature and favors stacking faulting, (nano)twinning and strain-induced martensite (SIM) formation, resulting in severe microstructural fragmentation. The effect of temperature on deformation behavior of AISI 317 L steel was investigated in samples rolled at room temperature to thickness reductions of 50% and 85% and at 77 K to reductions in thickness of 10% and 50%. The microstructural evolution was followed by scanning electron microscopy, Vickers microhardness, X-ray diffraction, magnetization, electron backscatter diffraction (EBSD) and electron channeling contrast imaging (ECCI). The nucleation sites in the early stages of the transformation sequence γ → ε → α' were identified in the 10% cryorolled sample. The highest volume fraction of α'-martensite reached 45.8% in the cryorolled steel to 50% rolling reduction. Much lower fractions were obtained for samples rolled to 10% reduction at 77 K (2%) and at room temperature to 50% (0.3%) and 85% reductions (1.6%). The texture components after cryorolling were Goss and Brass for austenite; rotated cube, α- and γ-fibers for δ-ferrite and α'-martensite. The ε-martensite presents the typical texture of hcp metals with a c/a ratio above the ideal value and 〈0001〉 − oriented tilted about 21° from the normal direction towards the rolling direction. The results show cryorolling as an effective method for enhancing SIM formation and promoting severe microstructural refinement in AISI 317 L stainless steel.

Influence of the martensitic transformation on the deformation behaviour of an AISI 316 stainless steel at low temperatures

Deformation microstructures and martensitic transformation pathways in cryogenically deformed 316L stainless steel

Modeling of the Kinetics of Strain‐Induced Martensite Transformation and the Transformation‐Induced Plasticity Effect in a Lean‐Alloyed Metastable Austenitic Stainless Steel

Influence of deformation-induced martensite on stress corrosion cracking of AISI 321 stainless steel

Strain-induced martensite formation in cryorolled AISI 317 L stainless steel

Effect Of Strain Rate On The Deformation-Induced Martensite Transformation And Mechanical Behavior Of Austenitic Stainless Steels For Cold Stretched Pressure Vessels

Martensitic Phase Transformation from Non-isothermally Deformed Austenite in High Strength Steel 22Simn2tib

Effect of Severe Cold or Warm Deformation on Microstructure Evolution and Tensile Behavior of a 316L Stainless Steel

Role of Strain-Induced Martensitic Phase Transformation in Mechanical Response of 304L Steel at Different Strain-Rates and Temperatures

Grain-orientation-dependent Phase Transformation Kinetics in Austenitic Stainless Steel under Low-Temperature Uniaxial Loading

Unraveling the Effect of Deformation Temperature on the Mechanical Behavior and Transformation‐Induced Plasticity of the SUS304L Stainless Steel

Microstructural Evolution and Mechanical Properties of 6cr13 Martensitic Stainless Steel Subjected to Cold Rolling and Heat Treatments

Effects of Strain State and Strain Rate on Deformation-Induced Transformation in 304 Stainless Steel: Part I. Magnetic Measurements and Mechanical Behavior

Martensitic Transformation in AISI-316 Austenitic Steel During Thermomechanical Processing

Influence of phase transformations on the mechanical properties of austenitic stainless steels

Influence of temperature on tensile properties of T91 ferritic/martensitic steel

Temperature Dependence of Deformation Behaviors in High Manganese Austenitic Steel for Cryogenic Applications

Cryogenic Work-Hardening Behavior for a Metastable Austenitic Stainless Steel at Liquid Nitrogen Temperature

Breaking the Strength-Ductility trade-off in Austenitic Stainless Steel at Cryogenic Temperatures: Mechanistic Insights

TENSILE AND LCF PROPERTIES OF AISI 316LN SS AT 300 AND 77 K

Study on deformation-induced martensitic transformation behavior of 304 and 316 stainless steels