Abstract:In order to investigate the effect of heat treatment on the microstructure and tensile properties of an Mg-5Gd-4Y-0.5Zn-0.5Zr alloy, the phase diagram was calculated by Pandat software, and accordingly the as-extruded alloy was annealed at 450, 510 and 550 °C followed by water quenching. The microstructure and mechanical properties of the specimens were analyzed subsequently by X-ray diffraction, scanning electron microscopy, transmission electron microscopy and tensile testing. The results showed that the average grain size of the as-extruded specimen was about 4 μm, in which Mg24Y5 was detected, and fine-grain strip was formed during the extrusion process. The grain size of the specimen annealed at 450 °C for 24 h was about 11 μm, and the main secondary phases were 14H-LPSO, δ-Zr3Zn2, β1-Mg3Gd and (HCP)Zr particles. The plate-like 14H-LPSO and cubic β1- Mg3Gd phases were coherent with the matrix, and the surface layer of (HCP)Zr was enriched with Zn atoms. When the annealing temperature reached 510 °C and 550 °C, the grain size increased to about 83 and 151 μm, respectively. The 14H-LPSO phases were gradually dissolved while the other secondary phases still existed. It was shown by uniaxial tensile testing that the ultimate tensile strength (UTS), yield tensile strength (YTS) and elongation (EL) of the as-extruded specimen were 291 MPa, 236 MPa and 24.7%, respectively. Increase of UTS, EL and decrease of YTS was resulted after annealed at 450 °C. However, both the strength and ductility dropped obviously after annealed at 510 °C and 550 °C. Ductile fracture features were found on the fracture surface of the as-extruded and 450 °C annealed specimens, whereas brittle topology, such as cleavage, was the main feature on the fracture surfaces of the specimens annealed at higher temperatures. Based on the strength analysis, it was concluded that the fine-grain strengthening was more important than solution strengthening and precipitation strengthening in this work.

Synergetic Regulation of Microstructure, Mechanical Properties and Corrosion Resistance of As-Rolled Mg–3Y Alloy by Annealing Treatment

Effect of annealing treatment on the microstructure and mechanical properties of warm-rolled Mg–Zn–Gd–Ca–Mn alloys

Effects of annealing treatment on microstructure and tensile behavior of the Mg-Zn-Y-Nd alloy

Effect of Heat Treatment on Microstructure and Properties of Rolled Mg-4Y-3Nd-1.5Al Alloy

Effect of Annealing on Microstructure and Tensile Properties of As-Extruded Mg-5Gd-4Y-0.5Zn-0.5Zr Alloy

Strength-ductility balance of Mg-1.03Ca-0.47Mn Mg alloy sheet produced by rolling and annealing

Regulating microstructure and mechanical properties of the as-cast Mg-4Zn-0.5Y-0.5Nd alloy by heat treatment

Effect of annealing treatment on texture evolution, microstructure and mechanical properties of an extruded Mg-Gd-Zn-Zr alloy

Effect of rolling temperature on microstructure and mechanical properties of hot-rolled Mg-Al-Ca-Zn-Mn alloys

Influence of Hot Rolling on Microstructure, Corrosion and Mechanical Properties of Mg–Zn–Mn–Ca Alloy

The Dependence of Final Microstructure, Texture Evolution and Mechanical Properties of Al–Mg–Si–Cu Alloy Sheets on the Intermediate Annealing

Microstructure evolution and mechanical property of Mg-3Al alloys with addition of Ca and Gd during rolling and annealing process

Enhancing Strength-Ductility Synergy and Corrosion Residual Strength of Hot-Rolled Mg-2Zn-0.85Y Alloy

Microstructure and properties of AZ31 alloy by static recrystallisation at lower temperature

Effect of Rolling Treatment on Microstructure, Mechanical Properties, and Corrosion Properties of WE43 Alloy

Microstructure and mechanical properties synergistically enhanced via heat treatment modification of the as-extruded Mg-1.5Al-0.5Zn-0.2Y-0.2Ca alloy

Effect of Annealing Treatment on the Mechanical Properties and Corrosion Behaviors of 01570 Aluminum Alloy

Microstructure and Mechanical Properties of As-Cast and Heat Treated Mg-15Gd-3Y Alloy

Simultaneously Improving Strength and Ductility of Mg−3Li−8Gd−2Y−1.5Ag Alloy by Solution Treatment and Hot‐Rolling Process

Effect of Annealing on the Microstructure, Texture, and Properties of Cold-Rolled Ti50Ni47Fe3 Shape Memory Alloy Sheets

Annealing coordinates the deformation of shear band to improve the microstructure difference and simultaneously promote the strength-plasticity of composite plate