Abstract:A modified ZSM-5 zeolite (denoted as ZSM-5-M), which was synthesized using tetrapropylammonium hydroxide (TPAOH) and cetyltrimethylammonium bromide (CTAB) as dual templates, and the commercial ZSM-5 zeolite (denoted as ZSM-5-C), have been used to prepare the corresponding CuZSM-5 (M & C) catalysts containing 3 wt% Cu by ion exchange method. Compared to CuZSM-5-C catalyst, the CuZSM-5-M catalyst demonstrated remarkably higher catalytic activity at low temperatures (<450 °C) for selective catalytic reduction of NOx with NH3 both in the simulated exhaust and engine bench testing. The modified synthesis by the dual template with the product aged for a long time at room temperature, leads to the formation of the ZSM-5-M zeolite with much higher specific surface area (608 m2 g−1) and higher total pore volume (0.8880 cm3 g−1) due to the presence of more mesoporous pores. The X-ray diffraction results showed that ZSM-5-M maintained its typical MFI structure, while its crystallinity (84.1%) was lower than that of the ZSM-5-C zeolite. The characterization results by H2 temperature-programmed reduction and X-ray photoelectron spectra revealed that the higher redox properties of isolated Cu2+ ions combined with the high-dispersion CuO crystallites and Cu+ ions are likely the main cause for the excellent low-temperature activity of the CuZSM-5-M catalysts. The isolated active Cu2+ species and high-dispersion CuO crystallites had a stronger interaction with other atoms in CuZSM-5-M catalysts. The results from thermogravimetric analysis, temperature-programmed desorption of ammonia and in situ diffuse reflectance infrared Fourier transform spectroscopy demonstrated that ZSM-5-M is a strong Bronsted acid site and the CuZSM-5-M catalyst had a relatively higher exchange rate of Cu2+ and Cu+ ions and more Lewis acidic sites, giving it a high NH3 adsorption capacity. The strong Bronsted acid site might be another cause that results in the higher NH3-SCR performance of the CuZSM-5-M catalyst.

The Study on Cu-ZK-5 Catalyst of Copper Content Regulation and Anti-Propylene Poisoning Mechanism in NH3-SCR Reaction

The study on Cu-ZK-5 catalyst of copper content regulation and anti-propylene poisoning mechanism in NH 3 -SCR reaction

Synthesis and evaluation of mesopore structured ZSM-5 and a CuZSM-5 catalyst for NH3-SCR reaction: Studies of simulated exhaust and engine bench testing

Effects of Catalyst Physicochemical Properties on the Catalytic Activity of Cu Zeolite Selective Catalytic Reduction at Different Inlet Gas Conditions

The Study of C3H6 Impact on Selective Catalytic Reduction by Ammonia (NH3-SCR) Performance over Cu-SAPO-34 Catalysts

Mechanism of propene poisoning on Cu-SSZ-13 catalysts for SCR of NO x with NH 3

Inhibition of Cu-SSZ-13 for NH 3 Selective Catalytic Reduction by K/Na Poisoning

Effect of Cu loading on the performance and kinetics of Cu/SAPO-34 catalysts for selective catalytic reduction with NH3

Characterization of Commercial Cu-SSZ-13 and Cu-SAPO-34 Catalysts with Hydrothermal Treatment for NH3-SCR of NOx in Diesel Exhaust

Catalytic performances of Cu-ZK-5 zeolites with different template agents in NH 3 -SCR

Optimizing the distribution and proportion of various active sites for better NH3-SCR property over Cu/SSZ-13

NH3-SCR on Cu, Fe and Cu + Fe Exchanged Beta and SSZ-13 Catalysts: Hydrothermal Aging and Propylene Poisoning Effects

Insights into the active sites of copper species in CuO/SiO2 catalysts for NH3-SCR: Quantitative analysis and mechanism study

Inhibiting the Formation of Toxic HCN Induced by C3H6 Coexistence and Enhancing C3H6 Resistance of Cu-Zeolite in the NH3-SCR Reaction

Hybrid Cu-Fe/ZSM-5 Catalyst Prepared by Liquid Ion-Exchange for NOx Removal by NH3-SCR Process

A novel Cu-Mo/ZSM-5 catalyst for NOx catalytic reduction with ammonia

Optimization of isolated copper species on the NH 3 -SCR performance over Cu/SSZ-39 modified by ammonia water

Insights into the active sites of copper species in CuO/SiO 2 catalysts for NH 3 -SCR: Quantitative analysis and mechanism study

Micro-structured Cu-ZSM-5 catalyst on aluminum microfibers for selective catalytic reduction of NO by ammonia

A New Insight into Active Cu2+ Species Properties in One‐Pot Synthesized Cu‐SSZ‐13 Catalysts for NOx Reduction by NH3

Catalytic Performances of Cu/MCM-22 Zeolites with Different Cu Loadings in NH3-SCR