Abstract:The rust/metal structure is one of the multiphase and multiple interface complex systems. The corrosion under rust is the uppermost and longest form of metallic corrosion evolution process. It is difficult to accurately determine the electrochemical parameters because the existence of rust complicates the electrochemical corrosion process. Based on the result of the previous studies of quiescent seawater, the weight-loss method and different electrochemical tests such as polarization curves (PC), electrochemical impedance spectra (EIS) and linear polarization resistance (LPR) were carried out to study the corrosion behavior of A3 carbon steel immersed in flowing seawater for about 280 d. After very short immersing time, there is a thin yellow rust layer on carbon steel, but as time prolonged, the yellow corrosion products are rushed away quickly, and a tense black rust layer cover about the whole electrode. The corrosion rate obtained by weight-loss method show a steady decline and keep stable after about 84 d, but it is higher than that of the static state system data. The cathodic polarization curves show an obvious reduction current peak at about -950 mV, which makes a remarkable overestimating of the cathodic corrosion current. Polarization resistance (R-p), determined by LPR and EIS, increases during the merely short-initial immersion period, then, it decreases gradually with immersion time. This means that the corrosion rate determined by electrochemical tests shows an another pattern compared with the weight-loss result. After a very short immersion time (about 14 d), there is a remarkable deviation between the weight-loss and electrochemical test results, and the longer immersed the greater of this deviation is. So no matter in static state or flowing seawater, electrochemical methods can not get an accurate corrosion rate of carbon steel. And reliable electrochemical measurement and analysis for rusted steel need much more attention.

Characterization of Corrosion Behavior and Corrosion Production Property of 90-10 Cupronickel Welding Joints in Flowing Seawater

Multiscale characterization of seawater pipe erosion of B10 copper-nickel alloy welded joints

The Corrosion Resistance of 0cr19ni9 Stainless Steel Arc Welding Joints with and Without Arc Surface Melting

Insight into the corrosion susceptibility and failure mechanism of Cu-Ni alloy pipeline welded joints in simulated marine environment

Insight to corrosion mechanism of 90/10 copper-nickel alloys under different sea depths

Probing the Anti-Corrosion Behavior of X65 Steel Underwater FSW Joint in Simulated Seawater

Corrosion of Copper-Nickel Alloys in Seawater-Based Electrolytes

Erosion–Corrosion Behavior of Friction Stud Welded Joints of X65 Pipelines in Simulated Seawater under Different Flow Rates

Corrosion Behavior of 16mnr Steel and Welded Joints in High-Temperature Naphthenic Acid

Corrosion behavior of austenitic stainless steel and nickel-based welded joints in underwater wet welding

Characterization of Flow-Accelerated-corrosion of Pressure Piping Welded Joints

Corrosion Behavior of High Strength Steel Welded Joint in Seawater: A Combinatorial Study Based on General and Localized Electrochemical Methods

Interhemispheric Functional Brain Connectivity in Neonates with Prenatal Alcohol Exposure: Preliminary Findings.

Corrosion behavior of the high‐strength low alloy steel welded joint in natural seawater

Corrosion Behavior of Long-Time Immersed Rusted Carbon Steel in Flowing Seawater

Long-Term Corrosion Behavior of Cu-10Ni and Cu-20Ni Alloys in Simulated Seawater

Corrosion resistance and mechanism of X100 pipeline steel laser-metal active gas hybrid welds with Cr containing welding wire in NS 4 solution

Characterization of Corrosion Behavior of TA2 Titanium Alloy Welded Joints in Seawater Environment

Electrochemical and Stress Corrosion Mechanism of Submarine Pipeline in Simulated Seawater in Presence of Different Alternating Current Densities

Corrosion Behavior of Ni/NiCr/NiCrAlSi Composite Coating on Copper for Application as a Heat Exchanger in Sea Water

Microscopic investigation on pitting corrosion of Ni-Cr-Mo-V high-strength steel weldment in simulated deep-sea environment