Corrosion behavior of austenitic stainless steel and nickel-based welded joints in underwater wet welding

Leandro Vaccari,Thomas Scheithauer,Ivan Lendiel,Jan Klett,Thomas Hassel,Hans Jürgen Maier

DOI: https://doi.org/10.1038/s41529-024-00471-9

2024-05-12

npj Materials Degradation

Abstract:Marine structures such as ports, bridges, pipelines, vessels, and platforms are an essential part of modern infrastructure, where the use of higher-strength steel provides savings in logistics and construction. However, the repair of higher-strength steels can be challenging, especially underwater. Wet shielded metal arc welding is the most widely used and least expensive method for underwater welding repairs, but is very susceptible to hydrogen-induced cracking. Thus, researchers and welding engineers aim to reduce the amount of hydrogen in the weld material. Recent success has been achieved through the use of austenitic welding consumables, such as austenitic stainless steel and nickel-based electrodes. The use of these consumables drastically reduces the amount of diffusible hydrogen in the weld metal. However, these austenitic materials usually have different corrosion potential as compared to the structural steel the weld beads are applied to. This creates the risk of severe galvanic corrosion. In the presented study, the corrosion behavior of welds created with austenitic stainless steel and nickel-based electrodes were studied. Samples were aged for 1.5 years in the Baltic Sea. Simultaneously, the effectiveness of corrosion protection systems such as coating and Impressed Current Cathodic Protection (ICCP) were evaluated. Localized corrosion occurred in the heat-affected zone when austenitic electrodes were used in the corrosive environment. The localized corrosion depth after 1.5 years in the Baltic Sea and in the salt spray layer was approximately 250 μm and 390 μm, respectively. The ICCP system and the use of a coating were effective in preventing localized corrosion. The low pitting corrosion density of 2.5 × 10 3 m −2 corresponds to grade A1 according to the standard and was found to be negligible as compared to the localized corrosion in the heat-affect zone.

materials science, multidisciplinary

What problem does this paper attempt to address?

The paper mainly addresses the following issues:

1. **Corrosion behavior of welding materials in underwater wet welding**: The study investigates the corrosion behavior when using austenitic stainless steel and nickel-based electrodes for underwater wet welding repair of high-strength steel. This is particularly examined after 1.5 years of immersion in the Baltic Sea and exposure to a salt spray environment.

2. **Differences in corrosion potential of different welding materials**: Austenitic stainless steel and nickel-based weld materials have different corrosion potentials compared to structural steel, which may lead to severe galvanic corrosion.

3. **Effectiveness of corrosion protection systems**: The effectiveness of coatings and impressed current cathodic protection (ICCP) systems in preventing localized corrosion was evaluated. The results show that these methods can effectively prevent localized corrosion.

4. **Depth of localized corrosion**: The study found that after 1.5 years of immersion in the Baltic Sea, the depth of localized corrosion was approximately 250 μm; after 720 hours of exposure in a salt spray environment, the depth of localized corrosion was approximately 390 μm.

5. **Pitting corrosion density**: Although there is a small amount of pitting corrosion (2.5 × 10^3 m^-2), its impact is relatively minor compared to localized corrosion.

Through these studies, the paper aims to provide theoretical basis and technical support for underwater wet welding repair of high-strength steel structures and propose effective anti-corrosion measures.