Abstract:s Mullite whiskers were synthesized based on the S-L-S growth mechanism at high temperatures using nano-alumina sol and nano-silica sol as the main materials and ammonium molybdate tetrahydrate as an additive. The effects of the silica-aluminum ratio, addition of ammonium molybdate catalyst, sintering temperature, and sintering time on the generation of mullite whiskers were systematically investigated to determine the optimal synthesis conditions. It was shown that the best raw material formulation was (3Al 2 O 3 ·2.2SiO 2 ) 8 (MoO 3 ) 2 , which minimized the mass loss of precursor powder at 0–1200°C, with only 23.62%. The mullite whiskers generated by sintering for 1–3 h maintained good microforms without agglomeration. The optimal growth conditions were 1300°C sintering for 1 h. The resulting mullite whiskers grew along the [240] direction and had the largest aspect ratios up to 10.2–14.3. The highest generation rate was up to 94.5 wt% with a grain size of 81.6 nm. The BET surface area was 2.308 m 2 /g and the pore size was 5.44 nm. The mass loss at 0–1200°C was the least, only 1.32%, with good thermal stability. In addition, the effects of (xAl 2 O 3 ·ySiO 2 ) 8 (MoO 3 ) 2 (x:y=3:1.8, 3:2, 3:2.2) whiskers treated at 1300°C on the APSB adhesive and MSABS adhesive bonding were investigated in this paper, it was clear that whiskers with x:y=3:2.2 had the best enhancement effect. For APSB adhesive strength could be increased by up to 55% and the fracture displacement by 2.42 times. For MSABS adhesives, the strength could be increased by up to 47% and the fracture displacement by 1.49 times.

Effect of Urchin-Like Mullite Whiskers on the High-Temperature Performance of Porous SiO<sub>2</sub>-Based Ceramic Molds

Effect of Urchin-Like Mullite Whiskers on the High-Temperature Performance of Porous SiO₂-Based Ceramic Molds.

Effect of in Situ Synthesised Mullite Whiskers on the High-Temperature Strength of Al2o3-Based Ceramic Moulds for Casting Hollow Turbine Blades

The effect of SiC whisker on the performances of Al2O 3 matrixceramics mould for hollow turbine blade

Analysis of Factors Affecting the Preparation of Mullite Whiskers from Silica-Rich Slag and Application Studies

Microstructure and Properties of Porous Anorthite/mullite Whiskers Ceramics with High Porosity

Effect of Heating Parameters on Sintering Behaviors and Properties of Mullite Whisker Frameworks

Significantly improved mechanical properties of mullite ceramics by adding AlOOH with different sizes and morphologies

Microstructures and High-Temperature Strength of Gel-Casting Al2O3-based Ceramic Molds with Coated Aluminum Additive

Effect Of Alumina-Based Fiber On The Mid-Temperature Strength Of Integral Ceramic Mold For Casting Hollow Turbine Blade

The preparation of mullite foamed ceramics reinforced by in-situ SiC whiskers and their reinforcement mechanism

The effect of multiple factors on the synthesis of mullite whiskers based on the S-L-S mechanism and the comparison of strengthening performance

The Effect of SiC Whisker on the Sintering and Thermal Shock Resistance Property of ZrO2-mullite Ceramic

High-temperature Strengthening Manufacturing of Alumina-based Ceramic Molds Used for Hollow Turbine Blades

Low sintering shrinkage and high strength of porous mullite–zirconia ceramics: Effect of AlF3 and ZrSi2 contents

A novel sintering additive system for porous mullite-bonded SiC ceramics: High mechanical performance with controllable pore structure

Effects of Adding Aluminum Oxide or Zirconium Oxide Fibers on Ceramic Molds for Casting Hollow Turbine Blades

Microstructure and Property of Porous Mullites with a Whiskers Framework Obtained by a Sol–gel Process

Microstructure and Crystallization Kinetics of Silica-Based Ceramic Cores with Enhanced High-Temperature Property

Effect of Chemical Vapour Infiltration Technique on the Gradient Microstructure and High-Temperature Strength of Gel-Cast Al2O3-based Ceramic Moulds

Near‐net‐size Preparation of Porous Mullite Matrix Ceramics with in Situ Formed 3D Mullite Whisker Network