Abstract:The ceramic core plays an important role in the preparation of aero-engine hollow blades, as it can directly determine the precision and pass rate of the cooling passage in the blade cavity. Sufficient high-temperature bending strength, high open porosity, and low sintering shrinkage are the main requirements for qualified ceramic cores. In order to prepare qualified ceramic cores with complex structures, in-situ mullite-reinforced Al2O3-based ceramic cores were successfully prepared using vat photopolymerization 3D printing technology. The in-situ synthesis of mullite was designed through thermodynamic analysis. The influence mechanisms of the sintering temperature and doping amount of fused silica on the open porosity, sintering shrinkage, and bending strength of the core were systematically investigated. With an increase in the sintering temperature and doping amount of fused silica, the porosity of the in situ mullite-reinforced ceramic core decreased. Sintering shrinkage increased with an increase in the sintering temperature and doping amount of fused silica. The cores containing 20 wt% fused silica showed the smallest sintering shrinkage. The bending strength increased with an increase in the sintering temperature and the doping amount of fused silica. A core doped with 20 wt% fused silica had the highest bending strength at 1773.15 K. Furthermore, 20 wt% fused silica doping, sintered at 1673.15 K, can be used to prepare in-situ mullite enhanced Al2O3-based cores with the best comprehensive properties. This core has a higher open porosity (40%), suitable bending strength of 25 MPa (at 1773.15 K), and lower sintering shrinkage in the Z direction. The significance of this study lies in the regulation of in-situ mullite generation and viscous flow in solid-liquid sintering by adjusting the doping amount of fused silica and the sintering process, and this opens up new pathways by the coordinated regulation of strength, open porosity, and sintering shrinkage of 3D printed ceramic cores.

Effect of Chemical Vapour Infiltration Technique on the Gradient Microstructure and High-Temperature Strength of Gel-Cast Al2O3-based Ceramic Moulds

Microstructure Evolution and Mechanical Properties of Ceramic Shell Moulds for Investment Casting of Turbine Blades by Selective Laser Sintering

Alumina-Based Ceramic Core Nano-Composites For Investment Casting

Influence of sintering temperature and CVI time on mechanical properties of 3D-printed alumina ceramics

FABRICATION OF POROSITY GRADIENT ALUMINA CERAMICS BY THE CENTRIFUGAL CASTING METHOD

Microstructure and Crystallization Kinetics of Silica-Based Ceramic Cores with Enhanced High-Temperature Property

Microstructure and properties evolution of silicon-based ceramic cores fabricated by 3D printing with stair-stepping effect control

Microstructure and mechanical properties of spark plasma sintered SiC–B4C gradient ceramics with Al additive

Improving the Homogeneity and Reliability of Ceramic Parts with Complex Shapes by Pressure-Assisted Gel-Casting

Enhanced 3D printed Al2O3 core via in-situ mullite

Ceramics with Special Porous Structures Fabricated by Freeze-Gelcasting: Using tert-Butyl Alcohol as a Template

Gel-casting for manufacturing porous alumina ceramics with complex shapes for transpiration cooling

Alumina-based ceramic mold with integral core and shell for hollow turbine blades fabricated by Laser powder bed fusion

Microstructure refinement-homogenization and flexural strength improvement of Al2O3 ceramics fabricated by DLP-stereolithography integrated with chemical precipitation coating process

Effect of sintering aid combined vacuum infiltration on the properties of Al 2 O 3 -based ceramics via binder jetting

Microstructure Evolution and Mechanical Behaviors of Alumina-Based Ceramic Shell for Directional Solidification of Turbine Blades

Microstructure Evolution of Ceramic Materials During Solidification from Melts in High-Gravity Combustion Synthesis

Effect of Sintering Temperature on Microstructure and Mechanical Behavior of Alumina-Based Ceramic Shell by SLS

Effect of Al(OH) 3 on the Properties of Silica-based Ceramic Cores Prepared by Laser Powder Bed Fusion Combined with Vacuum Infiltration

Preparation of high‐strength Si3N4 ceramics via vat photopolymerization: A bi‐phase particle size gradation strategy

Vat Photopolymerization of Sepiolite Fiber and 316L Stainless Steel-Reinforced Alumina with Functionally Graded Structures