Abstract:The effect of Sr content on the Al–7Si solidified microstructure was investigated. And the eutectic silicon modification level assessment of Al–7Si alloys was studied combined with the computer aided cooling curve pattern recognition method. It has found that the eutectic silicon modification level of Al–7Si alloy increases with the increase of Sr content. The eutectic structure is fully modified when the Sr content reaches 56ppm. While the modifier addition is given, the modification level decreases with the increasing of holding time. When the modifier addition is small, the modification level decreases with the increasing of holding time. But when the Sr addition is at a higher level, the modification level sustains at the initial period of holding time, and then decreases with the holding time. The results of modification level assessment show that the modification level difference converges to zero when the comprehensive parameter, which expresses the difference between cooling curves, approaches to zero. The whole shape of the solidification segment of a thermal analysis cooling curve can token the eutectic silicon modification level of the Al–7Si alloy melt. The modification level can be precisely assessed by comparison of the cooling curve of the melt to be evaluated with those in a database to find the one most similar to it. Based on a database established from a large amount of experimental results, the on-line prediction of eutectic modification level of Al–7Si alloy melt has been realized.

Assessment of Modification Level of Hypoeu- Tectic Al-Si Alloys by Pattern Recognition of Cooling Curves

Study on the Eutectic Modification Level of Al–7Si Alloy by Computer Aided Recognition of Thermal Analysis Cooling Curves

On-line prediction of aluminum–silicon eutectic modification level using thermal analysis

Quantitative Metallographic Analysis of Modification Level of Hypoeutectic Al-Si Alloys

Recognition of thermal analysis cooling curves and refinement of molten Al-7Si alloys

Pattern Recognition of Thermal Analysis Cooling Curves and Quality Evaluation of Melt Cast Alloys

Combined Treatment of Sr and B and Evaluation of Refinment-Modification Levels for Al-7si Casting Alloy

Modification mechanism and tensile property of Al-9Si-0.4Mg-0.1Cu alloy

Evaluating Melt Iron Features by Computer Aided Recognition of Thermal Analysis Cooling Curves

A numerical study of irregular eutectic in Al-Si alloys under a large undercooling

Intelligent Evaluation of Melt Iron Quality by Pattern Recognition of Thermal Analysis Cooling Curves

Effects of Refinement and Modification on Melt Structure of Hypoeutectic Al-Si Alloy

Effect of Ca Addition on Solidification Microstructure of Hypoeutectic Al-Si Casting Alloys

Quantifying the effects of cooling rates and alloying additions on the microporosity formation in Al alloys

Controlling Melt Quality of Compacted Graphite Iron

Incubation and Fading of Sr Modification in Hypoeutectic Al-Si Alloys

Effect of Cooling Rate on Solidification Parameters and Microstructure of Al-7Si-0.3Mg-0.15Fe Alloy

Effect of Scandium on Grain refinement mechanism and Mechanical Properties of Al-7Si-0.6Mg alloy at Different Cooling Rates

Effect of Cooling Rates on the Microstructure and Mechanical Property of La Modified Al7SiMg Alloys Processed by Gravity Die Casting and Semi-Solid Die Casting

Identification and evaluation of modification level for compacted graphite cast iron

Study on the eutectic and post-eutectic reactions in LM13 aluminum alloy using cooling curve thermal analysis technique