Simple fabrication of Cu2+ doped calcium alginate hydrogel filtration membrane with excellent anti-fouling and antibacterial properties

Tian Bai,Kongyin Zhao,Zijie Lu,Xuefang Liu,Ze Lin,Mengmeng Cheng,Ziyi Li,Dunwan Zhu,Linhua Zhang

DOI: https://doi.org/10.1016/j.cclet.2020.07.034

IF: 9.1

2021-03-01

Chinese Chemical Letters

Abstract:<p>Herein, copper ion doped calcium alginate (Cu²⁺/CaAlg) composite hydrogel filtration membranes were prepared by using natural polymer sodium alginate (NaAlg) as raw material. The thermal stability and structure of the composite membranes were characterized by thermogravimetric analysis and infrared spectroscopy. The mechanical strength, anti-fouling performance, hydrophilicity and filtration performance of the membrane were studied. The results show that Cu²⁺/CaAlg hydrogel membrane has excellent mechanical properties and thermal stability. The anti-swelling ability of the membrane was greatly enhanced by doping Cu²⁺. After three alternate filtration cycles, the flux recovery rate of Cu²⁺/CaAlg hydrogel membrane can still reach 85 %, indicating that the membrane has good anti-pollution performance. When the operation pressure was 0.1 MPa, the rejection of coomassie brilliant blue G250 reached 99.8 % with a flux of 46.3 L m⁻² h^-1, while the Na₂SO₄ rejection was less than 10.0 %. The Cu²⁺/CaAlg membrane was recycled after 24 h in the filtration process, and its flux and rejection rate did not decrease significantly, indicating that the hydrogel membrane has long-term application potential. The Cu²⁺/CaAlg membrane has a wide range of applications prospect in dye desalination, fine separation and biopharmaceutical technology fields.</p>

chemistry, multidisciplinary

What problem does this paper attempt to address?

This paper aims to solve the problems encountered in the application of traditional nanofiltration membranes in water treatment, especially the problems of membrane fouling and lack of antibacterial properties. Specifically, the authors prepared copper - ion - doped calcium alginate (Cu²⁺/CaAlg) hydrogel filtration membranes by a simple ion - cross - linking method to improve their mechanical properties, thermal stability, antifouling properties and antibacterial properties. This new membrane material has broad application prospects in the fields of dye desalination, fine separation and biomedical technology.

### Main problems solved in the paper:
1. **Membrane fouling problem**: Due to the hydrophobicity of the materials, traditional nanofiltration membranes are easily blocked by particles, colloids or solute macromolecules in water, resulting in membrane fouling and limiting the application of nanofiltration separation technology. To overcome this drawback, researchers have explored various methods to modify membrane materials and endow them with hydrophilicity, antifouling, self - cleaning, photocatalytic and photodegradation properties. In this paper, the antifouling property of the calcium alginate hydrogel membrane is improved by introducing copper ions.

2. **Insufficient antibacterial property**: Calcium alginate hydrogel itself does not have antibacterial properties and is easily swollen in monovalent ion solutions. By doping copper ions, not only the mechanical properties and thermal stability of the membrane are enhanced, but also the membrane material is endowed with excellent antibacterial properties.

### Experimental methods and results:
- **Preparation method**: Using the natural polymer sodium alginate (NaAlg) as a raw material, the Cu²⁺/CaAlg hydrogel filtration membrane was prepared by the ion - cross - linking reaction with calcium ions and copper ions.
- **Performance test**: The structure and properties of the membrane were characterized by Fourier transform infrared spectroscopy (FTIR), water contact angle measurement and thermal stability analysis. The experimental results show that the Cu²⁺/CaAlg membrane has excellent mechanical properties, thermal stability and anti - swelling ability.
- **Filtration performance**: Filtration tests were carried out on dye and salt solutions with different molecular weights. The results show that the rejection rate of the Cu²⁺/CaAlg membrane for macromolecular dyes is as high as 99.8%, while the rejection rate for small - molecule salts is less than 10%.
- **Antifouling performance**: The antifouling performance of the membrane was evaluated by alternately filtering pure water and yeast solution. After three consecutive filtrations, the flux recovery rate of the membrane can still reach 85%.
- **Antibacterial performance**: It was confirmed by the plate counting method and scanning electron microscope (SEM) observation that the Cu²⁺/CaAlg membrane has an antibacterial rate of 100%.

### Application prospects:
- **Dye desalination**: The Cu²⁺/CaAlg membrane has a high rejection rate for macromolecular dyes and is suitable for dye removal in textile wastewater.
- **Fine separation**: The membrane material performs well in drug separation and fine separation of biological samples.
- **Wastewater treatment**: In long - term operation, the flux and rejection rate of the membrane remain stable and are suitable for various wastewater treatment scenarios.

In conclusion, this research provides a simple method to prepare an efficient separation membrane with excellent antifouling and antibacterial properties, providing new solutions for fields such as dye desalination, fine separation and wastewater treatment.