Desalination of dye utilizing carboxylated TiO2/calcium alginate hydrogel nanofiltration membrane with high salt permeation

Xiao-lei Wang,Wei Qin,Li-xin Wang,Kong-yin Zhao,Hui-cai Wang,Hong-yu Liu,Jun-fu Wei
DOI: https://doi.org/10.1016/j.seppur.2020.117475
IF: 8.6
2020-12-01
Separation and Purification Technology
Abstract:<p>In order to recover dyes from textile wastewater, a self-supported carboxylated titanium dioxide/calcium alginate (TiO<sub>2</sub>-COOH/CaAlg) hydrogel nanofiltration membrane was prepared using TiO<sub>2</sub>-COOH as the reinforcing agent. The Scanning electron microscopy (SEM) and Energy dispersive X-ray (EDX) mapping scanning spectra were employed to characterize the distribution of TiO<sub>2</sub>-COOH nanoparticles on the membrane surface. The pore size distribution, zeta potential and mechanical performance of the membrane were evaluated. The rejections for single dye solutions, salt solutions and dye/salt mixture solutions were also examined. The results indicate that the TiO<sub>2</sub>-COOH nanoparticles are dispersed uniformly on the membrane surface. Compared to CaAlg membrane, the tensile strength of 20 wt% TiO<sub>2</sub>-COOH/CaAlg membrane is enhanced by 328%. At the operating pressure of 0.1 MPa, the rejection ratios of 20 wt% TiO<sub>2</sub>-COOH/CaAlg membrane for 100 mg/L Brilliant blue G250, Direct black 38 and Congo red are 98.4%, 96.8% and 95.9% respectively, and the permeate flux is about 14.1 L·m<sup>−2</sup>·h<sup>−1</sup>. Meanwhile, this membrane possesses the low rejection ratios for inorganic salts (16.1%, 15.6%, 12.3% and 9.0% for MgSO<sub>4</sub>, Na<sub>2</sub>SO<sub>4</sub>, MgCl<sub>2</sub> and NaCl, respectively), excellent dye anti-fouling property and good stability in the long-term filtration for dye/salt mixture solution.</p>
engineering, chemical
What problem does this paper attempt to address?