Abstract:Superconducting spherical shells may not only provide an appealing platform for exploring superconductivity in three-dimensional (3D) geometries with curved surfaces, but also be practically applied in important fields, such as in gyroscopes and gravimeters. In inertial confinement fusion (ICF), the perturbation on the target capsule caused by traditional contact support methods is recognized as one of the major contributors to performance degradation in ICF implosions. It was proposed recently that coating the capsule with a thin superconducting MgB2 spherical shell to realize non-contact support by means of magnetic levitation at the required temperatures similar to 20 K might offer a promising solution to this longstanding problem. To simulate the coating of ICF capsules, we deposited MgB2 spherical shells onto polycrystalline Si3N4 spheres (diameter d= 2 mm and 1 mm) via a hybrid physical-chemical vapour deposition technique. For both diameters, the spherical shells, of about 1 mu m in thickness and covering the whole spheres completely, were polycrystalline with thin plate-shaped MgB2 crystallites oriented randomly and closely connected. The spherical shells exhibited superconducting transition at a zero resistance temperature T-c(zero) c of 38.5-39.4 K in four-probe resistance measurements and ideal diamagnetism at low temperatures in magnetization measurements, suggesting the good crystallinity and homogeneity of the shells. The upper critical field H-c2, the irreversibility field H-irr and the lower critical field H-c1 were characterized and showed similar magnitudes and temperature dependencies for the d= 2 mm and 1 mm shells, yielding H-irr of 7-8 T and H-c1 of 7-12 mT at 20 K. The superconducting critical current density J(c) values, evaluated from the magnetization hysteresis loops, were 1.8x10(6) A cm(-2) and 8.5x10(4) A cm(-2) at 20 K under zero and 2 T applied field, respectively, for the d= 1 mm shell. The occurrence of small flux jumps was observed at low temperatures up to 12 K and in low fields below 0.3 T. The results demonstrate the feasibility of fabricating MgB2 spherical shells with properties applicable to potential areas employing magnetic levitation such as in ICF and that MgB2 spherical shells may be exploited as an experimental system to study superconductivity in 3D curvilinear geometry.

Spherical Superconducting $$\mathrm MgB_2$$ Thin Film

Properties of Superconducting MgB2 Spherical Shells Deposited on 2 Mm and 1 Mm Diameter Si3N4 Spheres

MgB2 Thick Films on Three-Dimensional Structures Fabricated by HPCVD

In Situ Epitaxial MgB2 Thin Films for Superconducting Electronics

GROWTH AND PROPERTIES OF SUPERCONDUCTING MgB_2 THIN FILM FABRICATED ON Al_2O_3 SUBSTRATE BY HYBRID PHYSICAL CHEMICAL VAPOR DEPOSITION

Thickness Dependenceof Superconducting Properties of MgB2 THIN FILMS on Al2O3 Substrates

SUPERCONDUCTING MgB2 FILMS FABRICATED ON STAINLESS STEEL SUBSTRATE BY HYBRID PHYSICAL CHEMICAL VAPOR DEPOSITION

MgB2 Superconducting Films Fabricated on Copper Substrate by Hybrid Physical-Chemical Vapor Deposition

Hybrid Physical-Chemical Vapor Deposition of Ultrathin Mgb2 Films on Mgo Substrate with High T-C and J(C)

Biaxial Strain Engineering on the Superconducting Properties of MgB2 Monolayer

Effect of Thickness on Properties of MgB2 Thin Films

MgB2films Fabricated on Molybdenum Substrate by Hybrid Physical–chemical Vapor Deposition for Superconducting RF Cavity Applications

Film Fabrication and Electronic Devices of MgB2 Superconductor

MgB2 thick film grown on Stainless steel substrate with ductility

Ultrathin Epitaxial Mgb2 Superconducting Films with High Critical Current Density and T-C above 33 K

Progress in Depositing MgB2 Films on Stainless Steel Substrate

Superconducting Mgb2 Thin Films On Silicon Carbide Substrates By Hybrid Physical-Chemical Vapor Deposition

MgB2 superconductor thin films on Si and Al2O3 substrates

Thin Film Magnesium Boride Superconductor with Very High Critical Current Density and Enhanced Irreversibility Field

Fabrication of superconducting magnesium diboride thin films by electron beam annealing