Abstract:In this work, the effect of rotary forward extrusion technique on the development of texture structure and mechanical anisotropy of Mg–12Gd–4Y–2Zn–0.4Zr sheets is studied. The experiments were carried out using a large-sized alloy (φ330 × 1100 mm) at an extrusion temperature of 460 °C and a high extrusion ratio (10.18). The average grain size of the alloy gradually decreases from 126.3 μm to 10 μm with increasing cumulative stress during rotary forward extrusion, the size of the second phase also decreases significantly and is uniformly distributed. At the same time, an abnormal texture (an abnormal extrusion texture with c-axis parallel to extrusion direction) parallel to the extrusion direction (ED) was formed by the rotation of grains, which was caused by the rotation of the basal plane along the principal stress axis driven by the continuous non-basal plane slip under high stress conditions. Dynamic recrystallized (DRX) also plays an essential role in the formation of the abnormal texture, where the DRX process produces a proportion of grains with the nucleation orientation . The subsequent preferential growth of these grains further promotes the rotation of the majority of grains oriented in the direction. Although the nucleation phase of DRX contributes to the formation of abnormal texture, the preferred growth stage of grains has a greater influence on the abnormal texture. In addition, due to the introduction of strong shear stresses, the degree of buckling and fragmentation of the Long Period Stacking Ordered (LPSO) phase is enhanced in all directions, which in turn reduces the morphological differences in different directions, ultimately leading to a significant weakening of mechanical anisotropy. This weakening of mechanical anisotropy is closely related to the homogeneity of the grain size and the differences in the morphology of the LPSO phases. Graphical

Analysis of Abnormal Texture and Strengthening Mechanisms of Extruded Mg–Gd–Y–Nd–Zr Alloy

Microstructure Evolution and Properties of Mg-9Gd-0.8Al Alloy with Lamellar Phase During Extrusion at Different Temperatures

Formation of Abnormal Texture and Anisotropy Weakening Mechanism of Mg–Gd–Y–Zn–Zr Sheets by Rotary Forward Extrusion

Texture, microstructure and mechanical properties of an extruded Mg-10Gd-1Zn-0.4Zr alloy: Role of microstructure prior to extrusion

Effects of extrusion process on microstructure, precipitates and mechanical properties of Mg-Gd-Y-Zr-Ag alloys

Dynamic Recrystallization and Texture Evolution of Mg–Y–Zn Alloy During Hot Extrusion Process

Dynamic Recrystallization, Texture Evolution, and Improved Mechanical Properties of Mg-Y-Zn-V Alloy during Forging and Subsequent Extruding Deformation

Texture tailoring and microstructure refinement induced by {11−21} and {10−12} twinning in an extruded Mg-Gd alloy

The synergistic and interactive effects of slip systems and dynamic recrystallization on the weakening basal texture of Mg-Y-Nd-Zr-Gd magnesium alloy

Influence of Extrusion Ratio on Microstructure and Tensile Properties of Mg–Gd–Y–Zn–Zr Alloy

Tuning texture and precipitation using Y/Gd atomic ratio in iso-concentration Mg–Y–Gd–Ag–Zr extruded alloys

Microstructure evolution, texture and mechanical properties of a Mg–Gd–Y–Zn–Zr alloy fabricated by cyclic expansion extrusion with an asymmetrical extrusion cavity: The influence of passes and processing route

Microstructure and mechanical properties of Mg-Gd-Zn-Zr alloy after hot extrusion

Effect of annealing treatment on texture evolution, microstructure and mechanical properties of an extruded Mg-Gd-Zn-Zr alloy

Non-Basal Slip Induced Rare Earth Texture Evolution in Mg-14Gd-0.5Zr (wt.%) Alloy During the Traditional Hot Rolling

Microstructure and Texture Evolution of Mg-Gd-Y-Zr Alloy during Reciprocating Upsetting-Extrusion

Understanding the weakening of texture in multiaxial forged ultrafine-grained strong and ductile Mg-2Zn-2Gd alloy

Achieving Enhanced Mechanical Properties of Extruded Mg-Gd-Y-Zn-Zr Alloy by Regulating the Initial LPSO Phases

Texture property and weakening mechanism of Mg-3Al-1Zn alloy by interactive alternating forward extrusion

Revealing the dynamic recrystallization mechanism, extrusion deformation mechanism, and tensile deformation behavior of Mg–6Al–1Zn–1.1Sc alloy

Microstructure evolution difference in Mg96.5Gd2.5Zn1 alloys extruded from as-cast and solution-treated states